The invention relates to the field of alloy, in particular to a corrosion-resistant aluminum alloy. A Aluminum Alloy corrosion, its ingredients include: Al, Si, Cu, Mn, Mg, which is characterized in that the weight ratio of Al was 93.7%95.4%, Si content and Cu content of 0.8%1.6% 2 to 4 per cent, the content of Mn is 0.2%0.4%, Mg content is 0.3%0.4%, this invention compared with the existing technology, system the preparation method is simple. The utility model has the advantages of good practicability and simple operation, and has good corrosion resistance at the same time that the aluminum alloy has high strength performance.
【技术实现步骤摘要】
一种耐腐蚀的铝合金本专利技术创造涉及合金领域,具体地说是一种耐腐蚀的铝合金。 铝合金由于强度高、重量轻、可挤压而被广泛应用在各工业领 域,铝合金在腐蚀环境中的问题之一为点腐蚀,腐蚀会造成铝合金制 品的完整性,可使铝合金制品失去功效。本专利技术创造的目的在于克服现有技术的不足,提供一种耐腐蚀性 强的铝合金。为实现上述目的,设计一种耐腐蚀的铝合金,其成份包括AL、 Si、 Cu、 Mn、 Mg,其特征在于配重比为AL 93.7%-95.4%Si 2%國4%Cu 0.8%-1.6%Mn 0.2%-0.4%Mg 0.3%-0.4%所述合金中其他杂质个元素含量为Fe 0-1%Cr 0-0.5%Ni 0-0.5%Co 0-0.5%Zn 0-1.5o/o V 0-0.2%本专利技术创造与现有技术相比,制备方法简单。成品实用性好,工 艺操作简便,在保证铝合金强度高的性能的同时,具有良好的耐腐蚀 性能。耐腐蚀的铝合金,其成份包括AL、 Si、 Cu、 Mn、 Mg,其特征在 于配重比为;AL 93.7%-95.4%Si 2%-4%Cu 0.8%-1.6%Mn 0.2%画0.4%Mg 0.3%-0.4%所述合金中其他杂质个元素含量为Fe 0國1%Cr 0-0.5%Ni 0-0.5%Co 0-0.5%Zn 0-1.5%V 0-0.2%权利要求1、一种耐腐蚀的铝合金,其成份包括AL、Si、Cu、Mn、Mg,其特征在于配重比为AL93.7%-95.4%Si2%-4%Cu0.8%-1.6%Mn0.2%-0.4%Mg0.3%-0.4%2、 根据权利要求l所述的一种耐腐蚀的铝合金,其特征在 ...
【技术保护点】
一种耐腐蚀的铝合金,其成份包括:AL、Si、Cu、Mn、Mg,其特征在于配重比为: AL 93.7%-95.4% Si 2%-4% Cu 0.8%-1.6% Mn 0.2%-0.4% Mg 0.3%-0.4% 。
【技术特征摘要】
【专利技术属性】
技术研发人员:杨成楼,
申请(专利权)人:上海鑫楼化学品配载有限公司,
类型:发明
国别省市:31[中国|上海]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。