The invention relates to a high sulfur content in iron desulfurization agent production method, the iron oxide desulfurizer consists of cubic phase Fe: 3 O: 4, Fe: 2 amorphous O: 3 and 2: amorphous Fe O: 3.H: 2 O, which comprises the following steps: (a) the solid soluble ferrous salt and soluble carbonate mixture in the reactor, adding water, stirring the reaction after opening, the material in the mixing process further mixed reaction; (b) the step (a) into the product wash tank, wash the product using dissolved oxygen of water; (c) will get into the slurry after washing buffer tank, after the centrifugal separation; (d) will be separated from the solid in air drying or drying . The process can be used for mass industrial production of the high sulfur iron containing desulfurizer, and the efficiency is high.
【技术实现步骤摘要】
本专利技术涉及一种高硫容铁系脱硫剂的制造方法，特别适用于大规模工业 生产，属于脱硫剂
技术介绍
中国专利CN101134918A公开了一种具有高硫容的可用于从气态或者 液态物料中脱除硫化氢的脱硫剂活性组分，该脱硫剂活性组分包括立方晶 系晶相Fes04、无定形Fe203、无定形Fe203'H20。该脱石克剂创造性地选择 了常用的铁氧化物脱硫剂的晶相，巧妙地利用了上述各种不同晶相的氧化 铁之间的协同作用，实现了该脱硫剂的高硫容。有关该脱硫剂的制备方法， 其包括如下步骤(1 )将固体可溶性亚铁盐与固体氢氧化物，按铁与氢氧 根的摩尔比为1:2 ~ 1:3进行混合；(2 )将步骤(1 )所得混合物料通过混捏 完成反应；(3)将步骤(2)所得反应产物在空气中晾千；(4)对步骤(3) 所得物料水洗并过滤；(5)将步骤(4)所得固体自然干燥或烘干。在上述制备方法中，需要对混合后的反应物料进行混捏，虽然该混捏 过程可以通过混捏机进行，但是受到现有技术的限制，要在混捏机内完成 大批量的反应物料之间的充分混捏反应是需要很长时间的；此外，对于经 混捏后的物料还需要将其置于空气...
【技术保护点】
一种高硫容铁系脱硫剂的生产制造方法，所述铁系脱硫剂由立方晶系晶相Ｆｅ↓［３］Ｏ↓［４］、无定形Ｆｅ↓［２］Ｏ↓［３］和无定形Ｆｅ↓［２］Ｏ↓［３］.Ｈ↓［２］Ｏ组成，其包括如下步骤： （ａ）将固体可溶性亚铁盐与可溶性碳酸盐置于混料反应 器中，并加入适量水，之后开启搅拌，在搅拌过程中使上述反应物料进一步混合反应； （ｂ）将步骤（ａ）得到的产物送入水洗罐中，利用溶解有氧气的水对上述产物进行洗涤； （ｃ）将洗涤后得到的浆料送入缓冲槽中，之后对其进行离心分离； （ｄ）将分离得到的固体置于空气中晾干或烘干。
【技术特征摘要】
【专利技术属性】
技术研发人员：刘存芳，赵刚，
申请(专利权)人：北京三聚环保新材料股份有限公司，
类型：发明
国别省市：11[中国|北京]