具高耐热油特性的不粘涂料组合物制造技术

本发明专利技术提供一种具高耐热油特性的不粘涂料组合物，该组合物包括：（１）５０－８０ｗｔ％聚酰胺酸树脂，（２）３－２０ｗｔ％氟碳聚合物，所述氟碳聚合物选自聚四氟乙烯、四氟乙烯／全氟烷基乙烯基醚共聚物、四氟乙烯／六氟丙烯共聚物（ＦＥＰ）或其组合；（３）１０－４０ｗｔ％溶剂，和（４）１－１０ｗｔ％着色用色粉。本发明专利技术的涂料组合物可以得到具有良好的耐热性，尤其是耐热油性的硬化物涂层，可以应用在不粘炊具中，尤其是油炸锅。

Non stick coating composition with high heat resistant oil characteristics

The present invention provides a non stick coating composition of high oil properties, the composition includes: (1) 50 - 80wt% polyamic acid resin, (2) 3 - 20wt% fluorocarbon polymer, a fluorocarbon polymer selected from the group consisting of PTFE / tetrafluoroethylene perfluoroalkyl vinyl ether copolymer of tetrafluoroethylene and propylene copolymer (F / six FEP) or a combination thereof; (3) 10 40wt% solvent, and (4) 1 - 10wt% color toner. The coating composition of the present invention can obtain a hardened coating with good heat resistance, especially heat resistant oil, which can be applied in non stick cookware, in particular to a frying pan.

【技术实现步骤摘要】

本专利技术涉及一种涂料组合物，更具体涉及具高耐热油特性的不沾涂料组合 物。此涂料组合物主要用于油炸锅的不粘涂层，亦可以用于其它炊具的不粘涂 层。
技术介绍
因为氟碳树脂具有良好的耐化学性、耐热性及不粘性，因此经常被用来当作 金属的保护涂装。如不粘锅、电饭锅、油炸锅或其它需要耐腐蚀的化学装置等。目前，现有技术中氟碳树脂采用水性二涂聚四氟乙烯不粘涂料的形式涂覆 在金属表面。也即，所述水性聚四氟乙烯不粘涂料均为两层涂层。通常，水性 二涂聚四氟乙烯不粘涂料的组成物主要是聚四氟乙烯乳液，但因聚四氟乙烯的 熔融黏度高，因此在高温烘烤后，所形成的涂膜容易有针孔产生，造成皮膜有 缺陷，在煮热油的过程中，油会由针孔的地方渗进，而造成皮膜软化或掉漆，依 经验水性二涂聚四氟乙烯不粘涂料的长期耐热油性并不好，因此认为不适用于油炸锅，除非在面漆再加上第三层四氟乙烯/全氟烷基乙烯基醚共聚物(PFA)的 涂层，降低针孔，但此方式会使成本增加许多。而通常聚四氟乙烯乳液由全氟辛酸化合物(例如全氟辛酸胺)制备得到，因 此难以避免地聚四氟乙烯乳液中含有全氟辛酸杂质。最近这一两年来，国内对于聚四氟乙烯乳液所制成的不粘涂料本文档来自技高网...

【技术保护点】
一种具高耐热油特性的不沾涂料组合物，该组合物包括：　（１）５０－８０ｗｔ％聚酰胺酸树脂，　（２）３－２０ｗｔ％氟碳聚合物，所述氟碳聚合物选自聚四氟乙烯、四氟乙烯／全氟烷基乙烯基醚共聚物、四氟乙烯／六氟丙烯共聚物（ＦＥＰ）或其组合 ；　（３）１０－４０ｗｔ％溶剂，和　（４）１－１０ｗｔ％着色用色粉。

【技术特征摘要】

【专利技术属性】
技术研发人员：林学佐，陈冠青，袁文洋，钟迪克，
申请(专利权)人：慧智科技中国有限公司，
类型：发明
国别省市：32[中国|江苏]