制备具有自清洁性能的纤维织物的方法技术

一种纳米光催化领域的制备具有自清洁性能的纤维织物的方法，包括如下步骤：步骤一，将钛前驱物溶于醇中，形成溶液Ａ，在剧烈搅拌下把溶液Ａ滴加到稀硝酸中，持续搅拌，静置，得溶液Ｂ；其中，钛前驱物∶醇∶稀硝酸的体积比例为：１∶（２～１０）∶（２０～８０）；步骤二，将纤维织物浸没在溶液Ｂ中，热处理，得具有自清洁性能的纤维织物。本发明专利技术的方法在低温和酸性条件下，通过较长时间的搅拌和静置进行胶化处理，获得高活性锐钛矿水溶胶，随后通过纤维织物的浸渍处理获得具有自清洁能力的纤维织物，该纤维织物既可应用在环境领域和医学领域。

Method of making a fabric having self-cleaning properties

A nano photocatalysis preparation method of self-cleaning performance of fabric, including the following steps: 1, the titanium precursor is dissolved in the alcohol solution, the formation of A, with vigorous stirring the solution to A drops of dilute nitric acid, stirring, standing, to the solution B; in the titanium precursor: alcohol: dilute nitric acid volume ratio is 1: (2 ~ 10): (20 ~ 80); step two, the fabric heat treatment immersed in solution B, with self-cleaning performance of fabric. The method of the invention in low temperature and acidic conditions, by stirring a long time and are static gel treatment, high activity of anatase sol, followed by fiber fabric impregnated with self cleaning ability of the fabric, the fabric can be used in the field of environment and medicine.

【技术实现步骤摘要】

本专利技术涉及的是一种半导体光催化
的制备方法，特别是一种。
技术介绍
二氧化钛半导体光催化氧化技术使用的原料一二氧化钛价格低廉、性能稳定、无毒无腐蚀性；该技术可以利用太阳能为能源，而且反应条件温和、操作简便、无二次污染。其中的染料、表面活性剂、有机卤化物、农药、氰化物、酚类、多氯联苯和多环芳烃等，都能被有效地催化降解、脱色、去毒、矿化为无机小分子物质。二氧化钛粉末难于回收使该技术难以大规模应用。在现阶段实际应用中，Ti02光催化材料己用于水和空气的净化装置、自洁净玻璃表面、抗菌光催化陶瓷面砖等领域，产生了巨大的经济、环境和社会效益。但是二氧化钛主要固定在玻璃、二氧化硅、不锈钢、三氧化二铝等耐高温的基质上，在固定化过程中需要高温， 一方面需要大量的能耗，增加成本，另一方面，高温处理使得二氧化钛难以在耐温能力弱的基质如橡胶、纤维等的固定。玻璃纤维或碳纤维上负载Ti02的功能材料已有大量报道，但是涉及常规的溶胶凝胶无定形前驱物的后续高温热处理。纤维织物的光催化功能化的研究较少，但是具有显著的现实价值。而纤维织物的光催化功能化涉及低温制备高度晶化Ti02水溶胶技术，存在一定难度。经本文档来自技高网...

【技术保护点】
一种制备具有自清洁性能的纤维织物的方法，其特征是，包括如下步骤：　步骤一，将钛前驱物溶于醇中，形成溶液Ａ，在剧烈搅拌下把溶液Ａ滴加到稀硝酸中，持续搅拌，静置，得溶液Ｂ；其中，钛前驱物∶醇∶稀硝酸的体积比例为：１∶（２～１０）∶（２０～ ８０）；　步骤二，将纤维织物浸没在溶液Ｂ中，热处理，得具有自清洁性能的纤维织物。

【技术特征摘要】

【专利技术属性】
技术研发人员：蔡伟民，龙明策，吴德勇，
申请(专利权)人：上海交通大学，
类型：发明
国别省市：31[]