一种汽车底部导流板及其制造方法技术

本发明专利技术涉及一种汽车底部导流板，还涉及这种汽车底部导流板的制造方法。一种汽车底部导流板，其特征在于，用ＧＭＴ材料作为原材料制造而成。一种制造上述汽车底部导流板的方法，其特征在于，包括以下步骤：Ａ．将原材料ＧＭＴ，剪裁成两块小料，放入烘箱烘烤，烘烤温度２００℃～２４０℃，连续烘烤时间合计２５０ｓ～３００ｓ；Ｂ．将步骤Ａ烘烤熟化的ＧＭＴ迅速铺到模具上，按照模具形状铺料，两块小料分别铺放在左右两侧；Ｃ．铺料结束后合模，模具温度５０℃～９０℃，保压时间６０ｓ～８０ｓ，加压１５００Ｔ～２０００Ｔ；Ｄ．起模，取出产品定型。

Automobile bottom guide plate and manufacturing method thereof

The invention relates to an automobile bottom guide plate, and also relates to a method for manufacturing the bottom guide plate of the automobile. The utility model relates to a bottom guide plate of an automobile, which is characterized in that GMT material is used as raw material. A method of making the car bottom guide plate, which is characterized in that the method comprises the following steps: A. raw materials GMT, cut into two pieces of small material, into the oven baking, baking temperature 200 to 240 DEG C, continuous baking time total 250s ~ 300s; B. will step A GMT quickly spread to the baking curing mold according to the shape of the mold, material, two pieces of small material were placed on both sides; C. material after the end of mold, mold temperature 50 to 90 DEG C, the holding time of 60s ~ 80s, pressure 1500T ~ 2000T; D. die, remove the products.

【技术实现步骤摘要】

本专利技术涉及一种汽车底部导流板，还涉及这种汽车底部导流板的制造方法。
技术介绍
汽车底部导流板，使汽车底部结构光滑封闭，气流能够快速通过底部，减 少由于紊流导致的上升力，相当于增加了轮胎的抓地力，提高了整车高速行使 稳定性。目前国外的中高档汽车已基本在底部加装了汽车底部导流板，材质也从最 初的金属，发展到现在的纤维增强材料。国内的汽车底部导流板还刚刚起步，主要是金属和塑料材质。GMT是玻璃纤维毡增强的热塑性复合材料的英文縮略。
技术实现思路
本专利技术的目的的第一方面在于，提出一种汽车底部导流板，以解决现在的 汽车底部导流板存在的质量重、所用材料不可回收、影响环保、隔音效果不明 显等问题。一种汽车底部导流板，其特征在于，用GMT材料作为原材料制造而成。 与金属制成的汽车底部导流板相比，本专利技术采用GMT材料作为原材料制造 的汽车底部导流板具有以下优点1) GMT密度为1.12，金属中较轻的铝的密度为2.7，所以使用GMT材料作 为原材料制造汽车底板防护板符合当前汽车轻量化的趋势；2) 汽车底部导流板位于汽车底部，容易受到各种油性物质及水的侵袭，而3用GMT材料作为原材料制造的汽本文档来自技高网...

【技术保护点】
一种汽车底部导流板，其特征在于，用ＧＭＴ材料作为原材料制造而成。

【技术特征摘要】
1、一种汽车底部导流板，其特征在于，用GMT材料作为原材料制造而成。2、 一种制造权利要求1所述的汽车底部导流板的方法，其特征在于，包括 以下步骤A、 将原材料GMT，剪裁成两块小料，放入烘箱烘烤，烘烤温度200°C 240°C，连续烘烤时间合...

【专利技术属性】
技术研发人员：甘玮，郭海忠，梁恺，
申请(专利权)人：上海耀华大中新材料有限公司，
类型：发明
国别省市：31[中国|上海]