本发明专利技术属胶粘剂制备工艺领域，其特征在于：先将环氧树脂、丁基溶纤剂、ＯＰ－１０、聚乙烯醇溶液、硅酸钠依次混合，反应温度控制在３８－４０℃；再加入聚丙烯酸脂，反应温度控制在５０℃；待上述生成物冷却至２０－２５℃后加入聚酰胺；环氧树脂、丁基溶纤剂、ＯＰ－１０、聚乙烯醇溶液、硅酸钠、聚丙烯酸脂、聚酰胺的重量比依次为：（２５－５０）∶（２．５－１０）∶（５－１５）∶（７５－１５０）∶（１．５－３）∶（５０－１００）∶（２５－５０）。（*该技术在2019年保护过期，可自由使用*）

Preparation of waterborne anticorrosive adhesive.

The invention belongs to the technical field of adhesive preparation, which is characterized in that: the epoxy resin, butyl cellosolve, OP - 10, polyvinyl alcohol and sodium silicate are mixed, the reaction temperature is controlled at 38 - 40 DEG C; adding polyacrylic acid resin, the reaction temperature is controlled at 50 DEG C; the product is cooled to 20 25 degrees after adding polyamide; epoxy resin, butyl cellosolve, OP - 10, polyvinyl alcohol solution, sodium silicate, polyacrylic acid resin, polyamide weight ratio is as follows: (25 - 50): (2.5 - 10): (5 - 15): (75 - 150): (1.5 - 3): (50-100): (25 to 50).

【技术实现步骤摘要】

本专利技术属粘合剂制备工艺领域，特别涉及一种多层结构LIPN乳液互穿聚合物网络胶的制备工艺。原有同类产品，如近几年开发的EVA及聚丙烯酸脂类LIPN主要用于涂料(不包括带锈防腐涂料)及粘接剂，其适用范围受到一定限制。本专利技术的目的在于提供一种具有耐水、防腐、无毒、无污染，性能优良且适用范围广泛的水性防腐万能胶的制备工艺。本专利技术的技术解决方案可依如下方式实现一种水性防腐万能胶的制备工艺，其特征在于先将环氧树脂、丁基溶纤剂、OP-10、聚乙烯醇溶液、硅酸钠依次混合，反应温度控制在38-40℃；再加入聚丙烯酸脂，反应温度控制在50℃；待上述生成物冷却至20-25℃后加入聚酰胺；上述原料物环氧树脂、丁基溶纤剂、OP-10、聚乙烯醇溶液、硅酸钠、聚丙烯酸脂、聚酰胺的重量比依次为(25-50)∶(2．5-10)∶(5-15)∶(75-150)∶(1．5-3)∶(50-100)∶(25-50)。本专利技术具有多种功能，性能优良。单组份常温固化，使用方便；无毒、无污染、无刺激、耐水、防腐、粘接力强，使用寿命可达10年以上。下面详述本专利技术的最佳实施方案；实施方案1一种水性防腐万能胶的制本文档来自技高网...

【技术保护点】
一种水性防腐万能胶的制备工艺，其特征在于：先将环氧树脂、丁基溶纤剂、ＯＰ－１０、聚乙烯醇溶液、硅酸钠依次混合，反应温度控制在３８－４０℃；再加入聚丙烯酸脂，反应温度控制在５０℃；待上述生成物冷却至２０－２５℃后加入聚酰胺；上述原料物环氧树脂、丁基溶纤剂、ＯＰ－１０、聚乙烯醇溶液、硅酸钠、聚丙烯酸酯、聚酰胺的重量比依次为：（２５－５０）∶（２．５－１０）∶（５－１５）∶（７５－１５０）∶（１．５－３）∶（５０－１００）∶（２５－５０）。

【技术特征摘要】
1.一种水性防腐万能胶的制备工艺，其特征在于先将环氧树脂、丁基溶纤剂、OP-10、聚乙烯醇溶液、硅酸钠依次混合，反应温度控制在38-40℃；再加入聚丙烯酸脂，反应温度控制在50℃；待上述生成物冷却至20-25℃后加入聚...

【专利技术属性】
技术研发人员：王长海，
申请(专利权)人：王长海，
类型：发明
国别省市：89[中国|沈阳]