Ultrasonic irradiation method for preparation of polymer / inorganic nanoparticles composite material, which is characterized by ultrasonic dispersion, crushing, activation and trigger multiple roles, in the realization of inorganic nanoparticles in liquid phase nano dispersion at the same time, realize the polymerization of monomer on the surface of nanoparticles, to achieve stable and complex inorganic nanoparticles, preparation of the product nano composite latex polymer, coating layer thickness of 5 65mm, can be directly used for coating and adhesive; after separation, drying to obtain functional polymer / inorganic nano composite material.
【技术实现步骤摘要】
本专利技术涉及一种制备聚合物／无机纳米粒子复合材料的方法。聚合物／无机纳米粒子复合材料是将无机纳米粒子分散于聚合物基体中的一种纳米复合材料。由于结合了聚合物和无机纳米材料的优点，经济、有效地利用纳米粒子独特的光、电、热、磁、力、化学活性、催化等性能，近年来受到各国学者的高度重视，已成为材料领域的研究热点之一。但由于无机纳米粒子表面能极高，极易凝聚成团，通过一般的共混复合难以真正实现纳米粒子在聚合物基体中的纳米分散和纳米复合。为解决这一问题，人们主要采用以下几种方法(1)物理沉积法(2)前驱体法(3)纳米微粒原位生成法(4)插层复合法(5)超分子自组装形成纳米复合材料法(6)包裹聚合法(E．Bourgeat-Lami，Ｐh．Espiard，A．Guyot，Polymer，36(23)，4385，1995)。其中，包裹聚合法可选择性大、适用范围广，受到人们高度重视。但包裹聚合法的难点是(1)纳米粒子在聚合介质中的纳米分散(2)单体在纳米粒子表面的聚合。本专利技术的目的是针对现有技术的不足而提供一种超声辐照制备聚合物／无机纳米粒子复合材料的方法，其特点是将超声辐照...
【技术保护点】
超声辐照聚合制备聚合物／无机纳米粒子复合材料的方法。其特征在于： （１）将无机纳米粒子０．１～５份，单体５～２０份，溶剂７０～９０份及其它助剂０．２～５份加入超声辐照反应器中，再将超声波变辐杆插入反应器内， （２）通入氮气约２～１０分钟，通氮气速率为０．１～５０毫升／分钟，通循环水浴温度为１０－７０℃， （３）启动超声波仪，进行聚合反应，超声功率调节范围在５０－１５００ｗ，频率，２×１０↑［４］～１０↑［９］Ｈｚ，反应时间１０分钟～５小时。
【技术特征摘要】
1．超声辐照聚合制备聚合物／无机纳米粒子复合材料的方法。其特征在于(1)将无机纳米粒子0．1～5份，单体5～20份，溶剂70～90份及其它助剂0．2～5份加入超声辐照反应器中，再将超声波变辐杆插入反应器内，(2)通入氮气约2～10分钟，通氮气速率为0．1～50毫升／分钟，通循环水浴温度为10-70℃，(3)启动超声波仪，进行聚合反应，超声功率调节范围在50-1500w，频率，2×104～109Hz，反应时间10分钟～5小时。2．按照...
【专利技术属性】
技术研发人员：王琪，夏和生，张楚虹，廖勇勤，徐僖，
申请(专利权)人：四川大学，
类型：发明
国别省市：90[中国|成都]