The invention discloses a high efficiency, high modulus, low rebound and low alkali accelerator and a preparation method thereof. The accelerator comprises the following components by weight: 60 \u2011 70 parts of deionized water, 15-22 parts of accelerator, 6-8 parts of complexing agent, 4.5-5.5 parts of accelerator, 0.5-3 parts of coordination agent, 3-5 parts of regulator and 1.5-3 parts of stabilizer. The invention has good performance with concrete: the rebound rate of concrete spraying and construction effect are good; the initial setting time of the clean slurry is less than 5min, and the final setting time is less than 12min; the 1D compressive strength is 10.2mpa, and the 28d compressive strength ratio is more than 100%, and has good adaptability with different cements.
【技术实现步骤摘要】
高效高模量低回弹型低碱速凝剂及其制备方法
本专利技术涉及建材砼外加剂
，特别涉及应用于喷射混凝土中的低碱液体速凝剂。
技术介绍
市场现有速凝剂产品有碱(高碱)速凝剂和无碱速凝剂，有碱速凝剂虽然掺量低，但碱含量较高，致使后期强度严重损失；其次，有碱速凝剂适应性较差，且使用掺量和产品性能不稳定，易沉淀；再其次生产工艺耗能高，成本较高，且对施工人员伤害大；加之密闭涵洞使用时严重影响操作人员健康，给公司造成很大的信誉损失，丢失大量速凝剂使用客户。而无碱速凝剂掺量过高，成本大，适应性低，回弹大，施工性偶有不足。喷射混凝土是将预先配好的水泥、砂、石子、水和一定数量的外加剂，主要是借助压力或其他动力喷枪喷涂灌筑细石混凝土的施工技术，通过管道输送高速喷灌筑隧道内衬、墙壁、天棚等薄壁结构或其他结构的衬里以及钢结构上，并迅速硬化凝结形成在其表面的保护层。一般常用碱性速凝剂是指速凝剂碱(Na2O+0.658K2O)含量占速凝剂总质量的6％～25％，低碱速凝剂碱(Na2O+0.658K2O)含量占速凝剂总质量的1％～6％以下，无碱速凝...
【技术保护点】
1.一种高效高模量低回弹型低碱速凝剂，其特征在于，包括以下重量份的组分：去离子水60-70份、促凝剂为15～22份、络合剂为6～8份、促进剂为4.5～5.5份、配位剂为0.5～3份、调节剂3～5份、稳定剂1.5～3份。/n
【技术特征摘要】
1.一种高效高模量低回弹型低碱速凝剂，其特征在于，包括以下重量份的组分：去离子水60-70份、促凝剂为15～22份、络合剂为6～8份、促进剂为4.5～5.5份、配位剂为0.5～3份、调节剂3～5份、稳定剂1.5～3份。
2.根据权利要求1所述的高效高模量低回弹型低碱速凝剂，其特征在于：所述促凝剂为硫酸盐无机化合物。
3.根据权利要求2所述的高效高模量低回弹型低碱速凝剂，其特征在于：所述硫酸盐无机化合物为优质无铁硫酸铝、高聚合硫酸铝、硫酸铝钾中的一种或者多种以任意比例混合。
4.根据权利要求1所述的高效高模量低回弹型低碱速凝剂，其特征在于：所述络合剂为铝酸钠、氟化钠、铝酸钾中的至少一种，其中铝酸钠纯度为99％。
5.根据权利要求1所述的高效高模量低回弹型低碱速凝剂，其特征在于：所述促进剂为氟铝酸盐或氟硅酸盐。
6.根据权利要求5所述的高效高模量低回弹型低碱速凝剂，其特征在于：所述氟铝酸盐为氟...
【专利技术属性】
技术研发人员：陈杰，冉晋友，方世昌，田应兵，皮永奇，
申请(专利权)人：贵州石博士科技有限公司，
类型：发明
国别省市：贵州;52