含氮化硼荧光玻璃的紫外LED及制备方法技术

本发明专利技术公开了一种含氮化硼荧光玻璃的紫外LED及制备方法，所述含氮化硼荧光玻璃的紫外LED制备方法的步骤包括：配置浆料，丝网印刷并干燥，低温烧结，封装并固化。本发明专利技术提供了一种含氮化硼荧光玻璃的紫外LED及其制备方法，通过采用特定组分配比的荧光浆料，有效避免了蓝光危害，同时增强了紫外LED的整体散热效果，减缓了因有机聚合物老化而导致的光效降低情况。

UV LED and preparation method of fluorescent glass containing boron nitride

The invention discloses a UV LED containing boron nitride fluorescent glass and a preparation method thereof. The steps of the preparation method of the UV LED containing boron nitride fluorescent glass include: preparing slurry, screen printing and drying, sintering at low temperature, packaging and curing. The invention provides a UV LED containing boron nitride fluorescent glass and a preparation method thereof. By adopting a fluorescent slurry with a specific group distribution ratio, the blue light harm is effectively avoided, the overall heat dissipation effect of the UV LED is enhanced, and the light effect reduction caused by the aging of the organic polymer is slowed down.

【技术实现步骤摘要】
含氮化硼荧光玻璃的紫外LED及制备方法
本专利技术涉及半导体光电领域，特别是一种含氮化硼荧光玻璃的紫外LED及制备方法。
技术介绍
发光二极管是一种基于P-N结电致发光原理的半导体发光器件，在照明和背光显示领域得到了广泛的应用，如照明器件、汽车头灯、显示屏幕等。目前，现有技术中最常用的半导体显示技术手段是通过蓝光InGaN芯片激发黄色YAG荧光粉产生白光，即蓝光激发黄色荧光粉发出黄光，黄光与蓝光混合发白光，但是由于缺少红光成分，仅使用蓝光激发的技术手段很难获得高显色指数和低色温的高品质白光，其显示品质，很容易受荧光粉层厚度影响。同时，因为发射谱中有高强度的蓝光，而国际化标准组织已经对LED产品做了蓝光危害等级标准，这种蓝光会对人眼的造成危害，主要表现在导致近视、白内障以及黄斑病变的眼睛病理危害。在材料的稳定性方面，现有技术中将荧光粉颗粒与有机聚合物混合，再将此混合物涂覆在LED封装器件上，这种方式所述所制备出的LED器件不仅热稳定性差，而且在长期热辐射和紫外照射下容易发生老化变黄现象，从而导致白光LED光效降低和可靠性下降。因此需要提出一种新的本文档来自技高网...

【技术保护点】
1.一种含氮化硼荧光玻璃的紫外LED制备方法，其特征在于，步骤包括：配置浆料，丝网印刷并干燥，低温烧结，封装并固化。/n

【技术特征摘要】
1.一种含氮化硼荧光玻璃的紫外LED制备方法，其特征在于，步骤包括：配置浆料，丝网印刷并干燥，低温烧结，封装并固化。


2.根据权利要求1中所述的含氮化硼荧光玻璃的紫外LED制备方法，其特征在于，所述配置浆料的步骤包括：以质量份计，取0.1～0.2份的乙基纤维素溶于0.3～0.5份的松节油透醇中，充分溶解后加入0.4～0.5份的玻璃粉、0.1～0.2份红色荧光粉、0.05～0.10份的绿色荧光粉、0.02～0.04份的蓝色荧光粉以及0.15～0.25份的氮化硼粉末，混合均匀后作为浆料。


3.根据权利要求2中所述的含氮化硼荧光玻璃的紫外LED制备方法，其特征在于，所述丝网印刷并干燥的步骤包括：将所述浆料通过丝网均匀涂覆至透镜表面，并干燥处理。


4.根据...

【专利技术属性】
技术研发人员：王昊，梁仁瓅，张骏，陈景文，杜士达，戴江南，陈长清，
申请(专利权)人：苏州紫灿科技有限公司，
类型：发明
国别省市：江苏;32