The invention belongs to the field of solid waste resource utilization, and discloses a method for preparing an adsorption material by using a mobile phone protective film adhesive and the prepared adsorption material and application. The method is to wash the adhesive of mobile phone protective film with water and dry it to obtain product a; then place product a in a tubular furnace and carbonize it at 200-1000 \u2103 under the protection of inert gas to obtain product B; finally immerse product B in alkali solution and dry it to obtain adsorption material. The method of the invention is simple, fast and low-cost, and solves the technical defect of recycling the adhesive after recycling the base material of the waste mobile phone protective film in the prior art. The adsorption material of the invention can be applied in the field of volatile organic compounds purification.
【技术实现步骤摘要】
一种利用手机保护膜粘合剂制备吸附材料的方法及其制得的吸附材料和应用
本专利技术属于固体废弃物资源化利用
，更具体地，涉及一种利用手机保护膜粘合剂制备吸附材料的方法及其制得的吸附材料和应用。
技术介绍
当前智能手机深入家家户户，导致手机保护膜的消费量大增。由于手机保护膜具有极强的化学惰性，很难被空气或是微生物等自然降解，会逐渐累积而占用大量的空间，从而造成严重的环境问题。另一方面，废旧高分子材料作为一种廉价且丰富的资源具有很好的回收利用的价值。因此，资源化回收废旧手机保护膜的基材具有较大的经济效益和环境效益。目前手机保护膜的回收工艺会产生大量的废弃粘合剂，传统的粘合剂处理方法如焚烧法，填埋法会进一步带来二次污染。因此，研发出一种利用手机保护膜粘合剂制备吸附材料的方法，以期解决现有技术中废旧手机保护膜基材回收后粘合剂资源化利用的技术缺陷，成为了本领域技术人员问题。
技术实现思路
为了解决上述现有技术存在的不足和缺点，本专利技术首要目的在于提供一种利用手机保护膜粘合剂制备吸附材料的方法，用于解决现...
【技术保护点】
1.一种利用手机保护膜粘合剂制备吸附材料的方法，其特征在于，包括以下具体步骤：/nS1.将手机保护膜粘合剂用水冲洗预处理，烘干后得产物A；/nS2.将产物A放置于管式炉中，在惰性气体保护下200～1000℃碳化处理，得到产物B；/nS3.将产物B浸渍于碱溶液中，再烘干处理，得到吸附材料。/n
【技术特征摘要】
1.一种利用手机保护膜粘合剂制备吸附材料的方法，其特征在于，包括以下具体步骤：
S1.将手机保护膜粘合剂用水冲洗预处理，烘干后得产物A；
S2.将产物A放置于管式炉中，在惰性气体保护下200～1000℃碳化处理，得到产物B；
S3.将产物B浸渍于碱溶液中，再烘干处理，得到吸附材料。
2.根据权利要求1所述的利用手机保护膜粘合剂制备吸附材料的方法，其特征在于，步骤S1中所述冲洗的次数为1～10次。
3.根据权利要求1所述的利用手机保护膜粘合剂制备吸附材料的方法，其特征在于，步骤S1中所述烘干的温度为40～80℃。
4.根据权利要求1所述的利用手机保护膜粘合剂制备吸附材料的方法，其特征在于，步骤S2中所述惰性气体为氮气、氩气或氦气。
5.根据权利要求1所述的利用手机保护膜粘合剂制备吸附材料的方法，其特征在于...
【专利技术属性】
技术研发人员：陈江耀，陈灿辉，安太成，李桂英，
申请(专利权)人：广东工业大学，
类型：发明
国别省市：广东;44