The invention relates to a hydrated calcium silicate used for removing copper ion in waste water and a preparation method thereof, belonging to the field of heavy metal ion removal. Calcium silicate hydrate was prepared by hydrothermal synthesis with calcium acetate and 40% water glass as calcium and silicon sources. The results show that the removal rate of 50 \u2011 200mg / L copper ion is more than 80% at the speed of 150 \u2011 400R / min, the temperature of 20 \u2011 60 \u2103, the pH value of 1 \u2011 14 and the adsorption time of 30 \u2011 90min. The invention selects calcium acetate and water glass with wide source and low price as reactants, and the prepared hydrated calcium silicate is in amorphous state, with high purity, large output and stable and efficient copper ion removal rate.
【技术实现步骤摘要】
一种去除废水中铜离子的水化硅酸钙及其制备方法
本专利技术涉及一种水化硅酸钙的制备方法，具体涉及一种能够去除废水中铜离子的水化硅酸钙及其制备方法，属于重金属离子去除领域。
技术介绍
近年来，随着工业的不断发展，我国环境问题也面临着极大的挑战，大量地表水和地下水环境受到各种重金属，如铅，镉，铜，汞、锌、铬等的污染。由于重金属具有富集性，很难在环境中被降解，且通过生物链的累积容易导致各种生物性的紊乱，重金属污染问题形势严峻。虽然近些年来随着相关政策的出台，环境问题得到了很大程度的改善，但是目前随着工业污染和大气污染，不少重金属离子会进入大气，伴随着降水的过程进入地表水、地下水、土壤等，造成环境污染，进而威胁到人类身体健康。重金属污染主要来源于矿石开采、化工制造、冶炼、电镀等工厂的生产过程。在我国，铜资源储备并不大，但铜污染问题相对比较普遍，这主要是由于铜资源在开采、加工、使用等过程中会产生大量含铜废水，其铜离子含量可高达几百毫克每升。因此，必须采取有效经济的方法处理含铜废水。目前，去除水体中重金属的方法主要包括：化学沉淀法，吸附法...
【技术保护点】
1.一种用于去除废水中铜离子的水化硅酸钙的制备方法，其特征在于，包括以下步骤：/n(1)首先，将乙酸钙置于三角烧瓶中，加入去离子水使之完全溶解；/n(2)乙酸钙充分溶解后，将质量分数为40％的水玻璃按1mL/min的速度匀速滴加至乙酸钙溶液中，使钙硅质量比为0.8-2.0，保持温度30℃，转速600rpm下搅拌使其反应2h，并恒温沉化3-28d；/n(3)反应结束后将(2)中的产物洗涤、过滤多次，去除产物表面残余的杂质离子；/n(4)将步骤(3)得到的产物放在真空干燥箱，烘干至恒重，即得到水化硅酸钙产物。/n
【技术特征摘要】
1.一种用于去除废水中铜离子的水化硅酸钙的制备方法，其特征在于，包括以下步骤：
(1)首先，将乙酸钙置于三角烧瓶中，加入去离子水使之完全溶解；
(2)乙酸钙充分溶解后，将质量分数为40％的水玻璃按1mL/min的速度匀速滴加至乙酸钙溶液中，使钙硅质量比为0.8-2.0，保持温度30℃，转速600rpm下搅拌使其反应2h，并恒温沉化3-28d；
(3)反应结束后将(2)中的产物洗涤、过滤多次，去除产物表面残余的杂质离子...
【专利技术属性】
技术研发人员：崔素萍，刘世杰，郭红霞，郑焱，王亚丽，
申请(专利权)人：北京工业大学，
类型：发明
国别省市：北京;11