The invention discloses a method for preparing dry-mixed mortar material from vanadium-titanium magnetite tailings. Firstly, the vanadium-titanium magnetite tailings are rounded by impact milling, blended with water reducing agent and retarder in proportion, and then homogenized in a low-temperature micro-shock fluidization device. Finally, the dry-mixed mortar material is obtained by adding quantitative cement for eccentric spin agitation. The invention takes vanadium titanomagnetite tailings as the main raw material, realizes the preparation of dry mixed mortar by rounding treatment, homogenization of additives and spin agitation process, and greatly improves the utilization rate of vanadium titanomagnetite tailings.
【技术实现步骤摘要】
钒钛磁铁矿尾矿制备干混砂浆材料的方法
本专利技术涉及绿色建筑材料制备
，特别涉及一种钒钛磁铁矿尾矿制备干混砂浆材料的方法。
技术介绍
钒钛磁铁矿矿尾矿是一种多组分矿物，复杂组分使其难以直接应用，常需加入一些校正材料和低熔材料用于制造渗水砖、泡沫玻璃等建材，尾矿利用率较低，使其不易推广。因此，开辟一种新应用领域，以提高其利用率及工业适应性至关重要。干混砂浆材料是一种应用极为广泛的建筑材料。如何将钒钛磁铁矿矿尾矿利用制备干混砂浆材料未见相关的记载。
技术实现思路
本专利技术是针对常见手段难以提高磁铁矿尾矿工业利用率问题的研发领域现状，提供一种钒钛磁铁矿尾矿制备干混砂浆的方法。为达到以上目的，本专利技术是采取如下技术方案予以实现的：一种钒钛磁铁矿尾矿制备干混砂浆材料的方法，包括以下步骤：1)将钒钛磁铁矿尾矿经对向冲碾圆化处理后，与减水剂、缓凝剂按一定比例掺和，再置于低温微震流化装置中均化成粒；2)按一定比例称量处理后的尾矿粒与水泥，在偏心自旋翻搅装置中均匀化，最终制成干混砂浆材料。作为本专利技术的进一步改进，步骤1)中，对向冲碾圆化处理相对速度2000～2300°/分...
【技术保护点】
1.一种钒钛磁铁矿尾矿制备干混砂浆材料的方法，其特征在于，包括以下步骤：将钒钛磁铁矿尾矿经对向冲碾圆化处理后，与减水剂、缓凝剂掺和，再进行低温微震流化处理均化成粒，得到尾矿粒；圆化处理钒钛磁铁矿尾矿、减水剂、缓凝剂的质量百分比为(95～98)：(0.3～0.6)：(1.7～4.4)；取处理后的尾矿粒与水泥混合，均化处理钒钛磁铁矿尾矿与水泥的质量百分比(65～75)：(25～35)，再将混合物进行偏心自旋翻搅处理使其均匀化，最终制成干混砂浆材料。
【技术特征摘要】
1.一种钒钛磁铁矿尾矿制备干混砂浆材料的方法，其特征在于，包括以下步骤：将钒钛磁铁矿尾矿经对向冲碾圆化处理后，与减水剂、缓凝剂掺和，再进行低温微震流化处理均化成粒，得到尾矿粒；圆化处理钒钛磁铁矿尾矿、减水剂、缓凝剂的质量百分比为(95～98)：(0.3～0.6)：(1.7～4.4)；取处理后的尾矿粒与水泥混合，均化处理钒钛磁铁矿尾矿与水泥的质量百分比(65～75)：(25～35)，再将混合物进行偏心自旋翻搅处理使其均匀化，最终制成干混砂浆材料。2.如权利要求1所述的钒钛磁铁矿尾矿制备干混砂浆材料的方法，其特征在于，对向冲碾圆化处理相对速度2000～2300°/分，冲碾力30～50MPa。3.如权利要求1所述的钒钛磁铁矿尾矿制备干混砂浆材料的方法，其...
【专利技术属性】
技术研发人员：董洪峰，艾桃桃，李文虎，
申请(专利权)人：陕西理工大学，
类型：发明
国别省市：陕西,61