The invention discloses a silver-loaded zinc-containing composite nanosphere antimicrobial agent and a preparation method thereof. The silver-loaded zinc-containing composite nanosphere antimicrobial agent is obtained by dispersing the monodisperse zinc-containing composite nanosphere evenly in water, then slowly dropping silver saline solution to react, and evenly embedding cubic silver nanoparticles on the amorphous zinc-containing composite nanosphere antimicrobial agent. The synthetic material of the invention is simple, the method is simple, the reaction conditions are mild, the morphology of the product is uniform, the antimicrobial performance is excellent, and the method of the invention has low production cost and is suitable for industrial scale-up production.
【技术实现步骤摘要】
一种载银含锌复合纳米球抗菌剂及其制备方法
本专利技术属于纳米材料制备
，具体涉及一种载银含锌复合纳米球抗菌剂及其制备方法。
技术介绍
近年来，由于细菌对抗生素耐药性的日益增强，细菌感染已经成为严重的公共卫生问题之一。开发高效、环保、低成本的抗菌材料成为迫切的需要。其中，无机贵金属材料银(Ag)具有抗菌作用强、毒副作用小和不易产生耐药菌株等特点，在无机抗菌剂中居于主导地位。然而，Ag纳米粒子在热力学上是不稳定的，极易团聚使其表面能最小化，从而导致其抗菌活性大幅度降低。因此，构建载银的复合纳米抗菌剂，将银纳米粒子进行固定或稳定，克服其聚集问题，提升其抗菌活性具有重要的科学意义与社会效益。众多含银的无机或者有机复合纳米结构，因其特殊的结构组成和增强的抗菌性能而被应用于抗菌领域，如Ag/石墨烯聚合物水凝胶、Ag@金属有机骨架@羧甲基化纤维、Ag/ZnO、Ag/MgO、Ag/TiO2、Ag/CdS/ZnO等。《危险材料杂志》(Journalofhazardousmaterials，2018年，第342卷，第392-400页)首次报道了以单宁酸-金属聚合物层(PTA)包...
【技术保护点】
1.一种载银含锌复合纳米球抗菌剂的制备方法，其特征在于，包括如下步骤：称取500～600mg十六烷基三甲基溴化铵于50mL的圆底烧瓶中，加入30mL水超声分散均匀，再加入150～200mg锌盐、60～90mg六次甲基四胺和10～30mg抗坏血酸，然后将圆底烧瓶转移至油浴锅，在50～95℃下搅拌反应8～12h；反应完成后，自然冷却至室温，所得产物经离心洗涤，获得含锌复合纳米微球；称取20～60mg含锌复合纳米微球于50mL的圆底烧瓶中，加入20mL水超声分散均匀；将圆底烧瓶转移至油浴锅，在50～95℃下保温搅拌10min，再缓慢滴加完全溶解在10mL水里的1～20mg银盐，继...
【技术特征摘要】
1.一种载银含锌复合纳米球抗菌剂的制备方法，其特征在于，包括如下步骤：称取500～600mg十六烷基三甲基溴化铵于50mL的圆底烧瓶中，加入30mL水超声分散均匀，再加入150～200mg锌盐、60～90mg六次甲基四胺和10～30mg抗坏血酸，然后将圆底烧瓶转移至油浴锅，在50～95℃下搅拌反应8～12h；反应完成后，自然冷却至室温，所得产物经离心洗涤，获得含锌复合纳米微球；称取20～60mg含锌复合纳米微球于50mL的圆底烧瓶中，加入20mL水超声分散均匀；将圆底烧瓶转移至油浴锅，在50～95℃下保温搅拌10min，再缓慢滴加完全溶解在10mL...
【专利技术属性】
技术研发人员：钱海生，赵孟莉，张茂峰，王婉妮，储召友，
申请(专利权)人：合肥工业大学，
类型：发明
国别省市：安徽,34
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。