本发明专利技术涉及水泥技术领域，特别是一种环保水泥熟料，以石灰石为主料，按照质量份数计包括：石灰石105‑120份，煤灰渣25‑40份，铁粉3‑10份，环氧酯10‑15份，合成纤维10‑20份。其中，石灰石105份，煤灰渣30份，铁粉5份，环氧酯10份，合成纤维15份效果最好。采用上述配方后，本发明专利技术的水泥熟料通过环氧酯很好的提高水泥熟料整体的稳定性；另外，通过合成纤维很好的增强了水泥熟料的粘结力，提高了水泥熟料整体的性能。

An environmentally friendly cement clinker

The invention relates to the technical field of cement, in particular to an environmentally friendly cement clinker, with limestone as the main material. According to the number of parts, the clinker comprises 105 to 120 parts of limestone, 25 to 40 parts of coal ash slag, 3 to 10 parts of iron powder, 10 to 15 parts of epoxy ester and 10 to 20 parts of synthetic fibers. Among them, 105 were limestone, 30 were coal ash, 5 were iron powder, 10 were epoxy ester and 15 were synthetic fibers. After adopting the above formulation, the cement clinker of the present invention can improve the overall stability of the cement clinker by epoxy ester, in addition, the bonding force of the cement clinker is enhanced by synthetic fibers, and the overall performance of the cement clinker is improved.

【技术实现步骤摘要】
一种环保水泥熟料
本专利技术涉及水泥
，特别是一种环保水泥熟料。
技术介绍
水泥熟料以石灰石和煤灰渣、铁质原料为主要原料，按适当比例配制成生料，烧至部分或全部熔融，并经冷却而获得的半成品。在水泥工业中，最常用的硅酸盐水泥熟料主要化学成分为氧化钙、二氧化硅和少量的氧化铝和氧化铁。主要矿物组成为硅酸三钙、硅酸二钙、铝酸三钙和铁铝酸四钙。硅酸盐水泥熟料加适量石膏共同磨细后，即成硅酸盐水泥。中国专利技术专利CN103011633A公开了一种水泥熟料，所述水泥熟料由如下重量比的原料制成：石灰石75-85；电石渣15-20；黄沙岩5-15；铁粉2-5。此专利技术虽然很好的利用了电石渣，但是稳定性和粘结力不够。
技术实现思路
本专利技术需要解决的技术问题是提供一种稳定性好、粘结力强的水泥熟料。为解决上述的技术问题，本专利技术的一种环保水泥熟料以石灰石为主料，按照质量份数计包括：石灰石105-120份，煤灰渣25-40份，铁粉3-10份，环氧酯10-15份，合成纤维10-20份。进一步的，所述合成纤维为钢合成纤维、玻璃合成纤维、合成合成纤维、天然合成纤维中的一种。进一步的，石灰石105份，煤灰渣3本文档来自技高网...

【技术保护点】
1.一种环保水泥熟料，以石灰石为主料，其特征在于，按照质量份数计包括：石灰石105‑120份，煤灰渣25‑40份，铁粉3‑10份，环氧酯10‑15份，合成纤维10‑20份。

【技术特征摘要】
1.一种环保水泥熟料，以石灰石为主料，其特征在于，按照质量份数计包括：石灰石105-120份，煤灰渣25-40份，铁粉3-10份，环氧酯10-15份，合成纤维10-20份。2.按照权利要求1所述的一种水泥熟料，...

【专利技术属性】
技术研发人员：李颖聪，
申请(专利权)人：李颖聪，
类型：发明
国别省市：陕西,61