一种利用石膏废渣生产的通用水泥制造技术

本发明专利技术公开了一种利用石膏废渣生产的通用水泥,它包括以下重量份的各组分：熟料76‑82份、钙法脱氨工艺废渣2.5‑5份、天然石膏0‑5份、煤渣10‑19份、粉煤灰0‑5份以及助磨剂0.1‑0.2份；其中，所述钙法脱氨工艺废渣为钙法脱氨工艺中石灰乳脱硫酸铵后得到的废渣。本发明专利技术可将钙法脱氨工艺中石灰乳脱硫酸铵后得到的石膏废渣替代现有的水泥产品中的天然石膏作为水泥中的缓凝剂使用，成本相对较低又节能环保，实现废弃物的循环利用。

A General Cement Produced from Gypsum Waste Slag

The invention discloses a general cement produced by gypsum waste residue, which comprises the following components: clinker 76 parts, calcium deamination process waste residue 2.5 5 parts, natural gypsum 0 5 parts, coal slag 10 19 parts, fly ash 0 5 parts and grinding aids 0.1 0.2 parts. Among them, the calcium deamination process waste residue is the waste from lime milk deammonization process by calcium method. Slag. The gypsum waste residue obtained from the lime milk ammonium sulfate removal process in the calcium method deamination process can replace the natural gypsum in the existing cement products as a retarder in the cement, which has relatively low cost, energy saving and environmental protection, and realizes the recycling of the waste.

【技术实现步骤摘要】
一种利用石膏废渣生产的通用水泥
本专利技术涉及建筑材料领域，具体地说为一种利用石膏废渣生产的通用水泥。
技术介绍
水泥，粉状水硬性无机胶凝材料，加水搅拌后成塑性浆体，能在空气中硬化或者在水中更好的硬化，并能把砂、石等材料牢固地胶结在一起，它作为一种重要的胶凝材料，广泛应用于土木建筑、水利、国防等工程。我国具有丰富的石灰石矿产资源，但是我国是也一个天然石膏矿蕴藏量极为丰富的国家，到目前为止，建材行业中所用的石膏仍以天然石膏为主，此外，我国庞大的工业每年副产的石膏废渣较多，例如钙法脱氨工艺中石灰乳脱硫酸铵后得到的废渣基本上弃置未利用，它不仅消耗大量的矿产资源，还将产生新的二次污染。
技术实现思路
本专利技术的目的就是针对上述缺陷提供一种利用石膏废渣生产的通用水泥，它包括以下重量份的各组分：熟料76-82份、钙法脱氨工艺废渣2.5-5份、天然石膏0-5份、煤渣10-19份、粉煤灰0-5份以及助磨剂0.1-0.2份；其中，所述钙法脱氨工艺废渣为钙法脱氨工艺中石灰乳脱硫酸铵后得到的石膏废渣。钙法脱氨工艺废渣的水分为10%-12%。一种利用石膏废渣生产的通用水泥，它包括以下重量份的各组分：熟料80份本文档来自技高网...

【技术保护点】
1.一种利用石膏废渣生产的通用水泥，其特征在于它包括以下重量份的各组分：熟料76‑82份、钙法脱氨工艺废渣2.5‑5份、天然石膏0‑5份、煤渣10‑19份、粉煤灰0‑5份以及助磨剂0.1‑0.2份；其中，所述钙法脱氨工艺废渣为钙法脱氨工艺中石灰乳脱硫酸铵后得到的石膏废渣。

【技术特征摘要】
1.一种利用石膏废渣生产的通用水泥，其特征在于它包括以下重量份的各组分：熟料76-82份、钙法脱氨工艺废渣2.5-5份、天然石膏0-5份、煤渣10-19份、粉煤灰0-5份以及助磨剂0.1-0.2份；其中，所述钙法脱氨工艺废渣为钙法脱氨工艺中石灰乳脱硫酸铵后得到的石膏废渣。2.根据权利要求1...

【专利技术属性】
技术研发人员：罗容波，
申请(专利权)人：湖北荆工水泥股份有限公司，
类型：发明
国别省市：湖北,42