The invention discloses a method for preparing a high magnesium low heat cement clinker includes: 58% 65% high magnesium limestone; limestone 15% 21%; 5% 8% aluminum ore waste copper slag; 8% 12% 12% 15%; ash; mineral grinding into fine material, mixed into the preheater and preheating. The mixture after preheating into decomposition furnace, pulverized coal will be carried into the flameless combustion decomposition furnace, containing fly ash cement, the cement raw material into the rotary kiln, calcination temperature of 1300 DEG 1450 DEG C, rotation speed of the rotary kiln is 3.5 3.9r/min for cement clinker. The invention avoids the disadvantages of the traditional large amount of sulfide, has the advantages of high performance, low energy consumption and low carbon, saves the production cost, and reduces the emission of sulfide and carbon dioxide.
【技术实现步骤摘要】
一种高镁低热水泥熟料的制备方法
本专利技术涉及水泥熟料加工的
，特别是一种高镁低热水泥熟料的制备方法。
技术介绍
生产传统硅酸盐水泥的原材料主要是石灰质、粘土及其它硅、铝和铁质校正原料，水泥熟料的主要矿物成分为硅酸三钙、硅酸二钙、铝酸三钙和铁铝酸四钙。通常硅酸三钙占矿物组成的60～70％，硅酸二钙占15～25％，铝酸三钙占5～10％，铁铝酸四钙占10～15％。传统硅酸盐水泥熟料硅酸三钙矿物含量很高，不仅烧成温度很高，而且对石灰石的品位要求也很高，因此，传统水泥行业是典型的高排放、高能耗、高资源负荷的典型代表，是不可持续的。现有的水泥熟料加工通常是采用硫酸钙、硅酸二钙或硫铝酸钙等原材料制备而成，制备的过程中会产生大量的硫化废弃物，不仅污染环境，且给水泥熟料的生产提高了生产成本。专利申请号：201610614229.3公开一种低碳水泥熟料的制备方法及其应用方法，所述的低碳水泥熟料制备原料为含硅铝材料、石灰石及石膏，原料按一定比例混合均匀后进行粉磨形成生料，粉磨后生料粒径要求0.08mm方孔筛筛余小于10％，粉磨后的原料在煅烧温度1200-1300℃条件下煅烧20...
【技术保护点】
一种高镁低热水泥熟料的制备方法，其特征在于，由以下矿物的质量百分比组成：石灰石58%‑65%；高镁灰石15%‑21%；铝矿废石5%‑8%；铜矿渣8%‑12%；煤灰12%‑15%。
【技术特征摘要】
1.一种高镁低热水泥熟料的制备方法，其特征在于，由以下矿物的质量百分比组成：石灰石58%-65%；高镁灰石15%-21%；铝矿废石5%-8%；铜矿渣8%-12%；煤灰12%-15%。2.根据权利要求1所述一种高镁低热水泥熟料的制备方法，其特征在于，包括以下矿物的质量百分比组成：石灰石58%-65%；高镁灰石18%-30%；铝矿废石5%-8%；铜矿渣8%-12%；煤灰12%-15%。3.根据权利要求1所述一种高镁低热水泥熟料的制备方法，其特征在于，石灰石中MgO的含量为≤1.5%。4.根据权利要求1所述一种高镁低热水泥熟料的制备方法，其特征在于，高镁灰石中的MgO的含量为...
【专利技术属性】
技术研发人员：贾成群，李建海，张洪，李强平，任述均，李天泽，杨庚社，凌绪光，周军，
申请(专利权)人：四川嘉华锦屏特种水泥有限责任公司，
类型：发明
国别省市：四川,51