The invention discloses a tridentate pyridinium imide iron catalyst and its preparation method and application, which relates to the technical field of conjugated diene catalytic polymerization. The iron catalyst consists of a main catalyst and a promoter, the main catalyst is tridentate pyridinium imide iron complex, and the promoter is methyl aluminoxane or alkyl aluminium. The above-mentioned iron catalytic system exhibits high activity in isoprene polymerization. The obtained polymer has high molecular weight and narrow molecular weight distribution. At the same time, the micro-structure of the polymer can be controlled by adjusting the structure of the main catalyst. At the same time, the activity of the reaction depends on the main catalyst of different substituents and different kinds of co-catalysts.
【技术实现步骤摘要】
一种三齿吡啶亚胺铁系催化剂及其制备方法与应用
本专利技术涉及共轭二烯烃催化聚合领域,具体涉及一种三齿吡啶亚胺铁系催化剂,还涉及催化剂的制备方法与在异戊二烯聚合中的应用。
技术介绍
近年来,环境友好的后过渡金属催化烯烃聚合引起科学家们越来越多的关注。铁系催化剂因其环境友好性、经济性、生物相容性以及对极性单体具有较好的耐受性,在异戊二烯聚合中也得到广泛关注。目前铁催化剂催化异戊二烯聚合的含氮配体主要为N,N二齿吡啶亚胺类,但是关于在铁催化中心附近装载第三齿配位基团以调控金属中心的电子特性和空间形状,从而调控催化异戊二烯的活性与选择性的研究还未见报道。
技术实现思路
为解决上述问题,本专利技术提供一种三齿吡啶亚胺铁系催化剂及其制备方法与应用。首先,本专利技术提供一种三齿吡啶亚胺铁系催化剂,由主催化剂和助催化剂组成,主催化剂为三齿吡啶亚胺铁配合物,其通用结构式为其中,R1为苯基,取代苯基或烷基;R2为H,甲基,乙基或苯基;R3为氢,烃基(不限于甲基、乙基等),芳基(不限于苯基、其它多环芳基等)或者卤素取代基(Br-,Cl-等);X为N取代基,O取代基,S取代基中的一种;n为1 ...
【技术保护点】
1.一种三齿吡啶亚胺铁系催化剂,其特征在于:由主催化剂和助催化剂组成,主催化剂为三齿吡啶亚胺铁配合物,其通用结构式为
【技术特征摘要】
1.一种三齿吡啶亚胺铁系催化剂,其特征在于:由主催化剂和助催化剂组成,主催化剂为三齿吡啶亚胺铁配合物,其通用结构式为其中,R1为苯基,取代苯基或烷基;R2为H,甲基,乙基或苯基;R3为H,烃基,芳基或卤素取代基;X为N取代基,O取代基或S取代基中的一种;n为1或者2;助催化剂为甲基铝氧烷(MAO)或烷基铝AlR3,所述甲基铝氧烷结构通式为其中n为4-40的自然数,所述烷基铝为三甲基铝,三乙基铝或三异丁基铝中的一种;助催化剂中的铝元素与主催化剂中的铁元素的摩尔比为(100-2000):1。2.根据权利要求1所述的三齿吡啶亚胺铁系催化剂,其特征在于:所述三齿吡啶亚胺铁配合物结构式为以下结构式中的一种:3.一种权利要求1或2中所述的三齿吡啶亚胺铁配合物的制备方法,其特征在于:在无水DCM中,将三齿吡啶亚胺配体与无水FeCl2或无水FeCl3混合,三齿吡啶亚胺配体与无水FeCl2或无水FeCl3的摩尔比为1:1,室温下搅拌反应24-48h,经过后处理,最终干燥得到三齿吡啶亚胺铁配合物。4.根据权利要求3所述方法,其特征在于:所述三齿吡啶亚胺配体结构式为以...
【专利技术属性】
技术研发人员:王庆刚,荆楚杨,王亮,赵梦梦,咸漠,
申请(专利权)人:中国科学院青岛生物能源与过程研究所,
类型:发明
国别省市:山东,37