The ceramic coating of the invention is nanometer 10 - 100nm oxide, and nano oxide is obtained by Sol - geL sol - gel method. The compounds with high chemical components are used as precursors, and the raw materials are mixed evenly under the liquid phase, and the hydrolytic condensation reaction is carried out. A stable transparent sol system is formed in the liquid phase. The basic principle of ceramic coating film formation is the condensation reaction of body, the copolymerization between nano-oxide and organosilicon compound and the condensation reaction between organosilicon compound.
【技术实现步骤摘要】
室内建筑墙体陶瓷涂料
本专利技术属于涂料
,尤其涉及其于无机涂料组合物。
技术介绍
随着经济的快速发展,建筑内墙涂料不断演变和革新,也由于人们对环保越加重视,水性纳米无机涂料,因其无毒,不释放有毒有害气体,降解有害物质,同时释放负离子,净化空气,自洁杀菌,附着力强,高硬度,可擦洗而受到高度重视。
技术实现思路
专利技术目的本专利技术旨在改变有机涂料,有甲醛排放,有害溶剂挥发,易干裂脱落,不耐脏,不可擦洗等缺点。制备出新一代内墙陶瓷涂料。
技术实现思路
基料:40—70水:3—8颜料:20—40有机溶剂:20—40有机酸调节剂:2—10。一、涂料组成物本专利技术涂料由基料、有机溶剂、有机酸调节剂和有机硅氧化合物组成。基料基料也称成膜物质,它的主要作用是将颜、填料等粘接成一个整体,并赋予涂膜光泽、防腐等功能。本专利技术陶瓷涂料为纳米级10—100nm氧化物,纳米氧化物是采用Sol—geL溶胶—凝胶法制备而得,急用含高化学组份的化合物作前驱体,在液相下将这些原料均匀混合,并进行水解缩合化学反应,在液相中形成稳定的透明溶胶体系,在成膜过程中,基料发生共聚反应及自身的缩合反应,纳米氧化物与有机硅化合物之间的共聚及有机硅化合物之间的缩聚反应是陶瓷涂料成膜的基本原理。(1)纳米氧化物主要有氧化硅、氧化铝、氧化锆、氧化钛。(2)有机硅氧烷优选三甲/乙氧硅烷、苯基三乙氧基硅烷、正硅酸四甲/乙酯、甲基苯基二甲/乙氧基硅烷。颜料现在技术涂料中采用的均为无机颜料,由于体系的特殊性,颜料与体系的匹配性非常重要,具体体现在:一是颜料在强酸介质中要非常稳定,二是颜料中水溶性盐的含量要足够低, ...
【技术保护点】
1.一种室内建筑墙体陶瓷涂料,其特征在于水性纳米单组份各成分重量分为基料:40—70水:3—8颜料:20—40有机溶剂:20—40有机酸调节剂:2—10涂料体系PH值在2—5之间,其中基料为纳米氧化物和有机硅氧烷有机溶剂:包括醇类、醚类。
【技术特征摘要】
1.一种室内建筑墙体陶瓷涂料,其特征在于水性纳米单组份各成分重量分为基料:40—70水:3—8颜料:20—40有机溶剂:20—40有机酸调节剂:2—10涂料体系PH值在2—5之间,其中基料为纳米氧化物和有机硅氧烷有机溶剂:包括醇类、醚类。2.如权利1要求所述的涂料,其特征在于体系PH值优选在3—5之间,更优选在3—4之间。3.如权利1所述的涂料有机溶剂包括C1—C6烷基醇,具体包括甲醇,乙醇,异丙醇,一缩二乙二醇,三缩二乙二醇,乙二醇,丙二醇,以及乙二醇丁醚,丙二醇甲醚。4.如权利1所述的涂料,其特征在于纳米氧化物包括,氧化钛,氧化铝,氧化锆,氧化硅,其纳米氧化物粒径在1—150nm之间,最佳选择为20—80nm。5.如权利1要求所述的涂料,其颜料为钛白粉,铬铁黑,铜铬黑,钴蓝,钛镍黄,锶黄,铬黄,钼铬红,镉红,铬绿,碳黑,水母珠光颜料。6.如权利...
【专利技术属性】
技术研发人员:矫贺,赵华旗,矫振询,
申请(专利权)人:上海涂尊新材料科技有限公司,
类型:发明
国别省市:上海,31