The invention discloses a method for improving the strength performance of box board paper. The method is to add gamma-pentyl lactone to the waste paper pulp after being fully soaked and dispersed, and the treated pulp is washed clean with hot water, and then paper is made. The dosage of gamma-pentyl lactone is 0.5 1g/g absolute dry pulp, and the treatment conditions are as follows: liquid ratio 1:8 12, temperature 60 100 C, and treatment time 1 3;h. The waste pulp fiber is treated with gamma-pentyllactone, which can effectively enhance the bonding force between fibers and ultimately improve the strength performance of waste pulp. Moreover, the gamma-pentyl lactone used in the invention is a biomass-based product, which is non-toxic, degradable, environmentally friendly and pollution-free, and can be used as a new paper-making treatment agent.
【技术实现步骤摘要】
一种提高箱板纸强度性能的方法
本专利技术涉及制浆与造纸
,具体涉及一种提高箱板纸强度性能的方法。
技术介绍
箱板纸是一种重要的包装材料,广泛应用于各类商品的包装、运输。随着日常消费品(特别是大宗家具家电)用量的增加,人们对包装材料的数量和质量都有了更高的要求。目前,箱板纸中二次纤维的比例高达80%以上,由于二次纤维成分复杂,含有大量的细小纤维组分和阴离子杂质,在干燥过程中发生的不可逆角质化,极大地降低了成纸强度。造纸中常用阳离子淀粉和阳离子聚丙烯酰胺等增强剂来提高成纸强度性能,但这一类增强剂的使用容易引起阴离子垃圾的干扰,还会对抄纸过程带来一定的负面影响,如BOD含量增加,网部沉积物增多、成纸匀度变差等。因此,如何提高箱板纸强度、维持稳定的生产质量是改善包装纸企业竞争力的重要途径。γ-戊内酯作为生物质基平台化合物分子可由纤维素和半纤维素催化转化而成,具有无毒、可生物降解的特性。其物理化学性质包括分子量100g/mol,密度1.05g/mL,熔点-31℃,沸点207℃,与水以任意比例互溶。同时,γ-戊内酯的独特气味使其非常容易检测泄露,非常适用于规模化储存、运 ...
【技术保护点】
1.一种提高箱板纸强度性能的方法,其特征在于,所述方法为在充分浸泡、分散后的废纸浆中加入γ‑戊内酯处理,处理的浆料用热水洗涤干净,然后抄造纸张;所述γ‑戊内酯的用量为0.5‑1g/g绝干浆,处理条件为:液比1∶8‑12,温度60‑100℃,处理时间1‑3h。
【技术特征摘要】
1.一种提高箱板纸强度性能的方法,其特征在于,所述方法为在充分浸泡、分散后的废纸浆中加入γ-戊内酯处理,处理的浆料用热水洗涤干净,然后抄造纸张;所述γ-戊内酯的用量为0.5-1g/g绝干浆,处理条件为:液比1∶8-12,温度60-100℃,处理时间1-3h。2.根据权利要求1所述的提高箱板纸强度性能的方法,其特征在于,处理条件为:液比1∶10,温度80℃,处理时间2h。3.根据权利要求1所述的提高箱板纸强度性能的方法...
【专利技术属性】
技术研发人员:王强,刘姗姗,杨桂花,吉兴香,陈嘉川,
申请(专利权)人:齐鲁工业大学,
类型:发明
国别省市:山东,37
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。