The invention discloses a solid hazardous waste stabilization landfill process, which comprises the following steps: 1) putting solid waste into stabilization and solidification equipment, adding hydrated lime and water to regulate solid waste pH above 8, stirring uniformly to make solid waste slurry; 2) adding 1 3% water solution of heavy metal chelating agent of solid waste volume, stirring evenly; 3) maintaining in landfill maintenance area; Maintain for 5 to 7 days so that the stabilized solidified waste can be treated harmlessly after being cured and moulded. The landfill process of the invention is simple, effectively solves the problem of harmless disposal of low content arsenide waste, greatly reduces the amount of lime/cement in the common solidification scheme, and provides an effective scheme for landfill disposal of this type of waste.
【技术实现步骤摘要】
一种固体危险废物的稳固化填埋工艺
本专利技术涉及固体危险废物的填埋工艺，具体涉及一种固体危险废物的稳固化填埋工艺。
技术介绍
目前大多接收处理的填埋类废物中石油、煤化工行业产生的危险废物催化剂、吸附剂、活性炭，有很大部分此类废物有少量砷化物超标，对其进行无害化处置过程中必须对危险废物中砷进行稳定化固化后，才能进行填埋处置。目前主要使用常规石灰/水泥稳固化方法，但其难与砷化物形成不溶于水的稳定化合物，难对砷化物起到稳定化固化效果，且石灰/水泥的用量大，需要研究更有效的稳固化填埋方案。
技术实现思路
基于此，本专利技术提供一种固体危险废物的稳固化填埋工艺，尤其是少量砷超标的固体废物的稳定化填埋工艺。本专利技术通过如下技术方案实现：一种固体危险废物的稳固化填埋工艺，包括如下步骤：1）将固体废物投料到稳定化固化设备中，加入熟石灰和水调节固体废物pH在8以上，搅拌均匀使固体废物呈泥浆状；2）加入固体废物量的1-3%重金属螯合剂的水溶液，搅拌均匀；3）在填埋养护区养护5-7天，使稳定化固化废物养护成型后，可无害化处理。在其中一些实施例中，所述步骤1）中固体废物为石油、煤化工行业产...
【技术保护点】
1.一种固体危险废物的稳固化填埋工艺，其特征在于，包括如下步骤：1）将固体废物投料到稳定化固化设备中，加入熟石灰和水调节固体废物pH在8以上，搅拌均匀使固体废物呈泥浆状；2）加入固体废物量的1‑3%重金属螯合剂的水溶液，搅拌均匀；3）在填埋养护区养护5‑7天，使稳定化固化废物养护成型后，可无害化处理。
【技术特征摘要】
1.一种固体危险废物的稳固化填埋工艺，其特征在于，包括如下步骤：1）将固体废物投料到稳定化固化设备中，加入熟石灰和水调节固体废物pH在8以上，搅拌均匀使固体废物呈泥浆状；2）加入固体废物量的1-3%重金属螯合剂的水溶液，搅拌均匀；3）在填埋养护区养护5-7天，使稳定化固化废物养护成型后，可无害化处理。2.根据权利要求1所述的固体危险废物的稳固化填埋工艺，其特征在于，所述步骤1）中固体废物为石油、煤化工行业产生的固体危险废物。3.根据权利要求1所述的固体危险废物的稳固化填埋工艺，其特征在于，所述...
【专利技术属性】
技术研发人员：李伟，温源，张新卫，
申请(专利权)人：克拉玛依沃森环保科技有限公司，
类型：发明
国别省市：新疆,65