The invention discloses a corrosion-resistant polymer material, which is made of the following components: polyaromatic ether grease: 50 80 copies; polybutylene: 10 20 copies; PET: 5 20 copies: ferric tetroxide: 5 10 copies; ferric oxide: 1 5 copies; copper oxide: 1 5 copies; magnesium oxide: 1 5 copies; and the contents of ferric tetroxide, ferric oxide, copper oxide and magnesium oxide are 800 2000 Eye. The corrosion-resistant macromolecule material of the invention can withstand the erosion of strong acids or oxidants such as concentrated sulfuric acid, concentrated hydrochloric acid, chlorine-containing solvents, and the service temperature is also higher than that of ordinary macromolecule materials. In addition, the cost of the invention is lower than that of general polymer materials, and the production process is all existing technology, which is especially suitable for industrial production.
【技术实现步骤摘要】
一种耐腐蚀高分子材料
本专利技术属于高分子材料
，具体涉及一种耐腐蚀高分子材料。
技术介绍
腐蚀是指材料与外界反应引起的材料破坏或变质，发达国家腐蚀损失平均占国民经济总收入2-4％。美国于1990年调查表明化学工业的腐蚀损失达829亿美而我国在腐蚀损失方面也做过调查。l988估计为270—500亿人民币。近年来，国内外大量应用实例表明，高分子材料在企业防腐领域中显示出越来越大的作用，并且以其易成型加工。易修补价格艇宜的优势越来越受人们的重视。因此国内外专家学者的研究工作也很活跃，新材料不断出现，为各行各业的实际应用提供了较多的选择机会。在一定温度下，高分子材料耐无机酸、碱、盐的腐蚀性能优于金属材料并随着科研工作的深入开展，高分子材料在防腐蚀领域中将发挥更大的作用。高分子材料的品种繁多，耐腐性能优异因而发展迅速，主要有热塑性树脂。热固性树脂和弹性体，热塑性树脂中仍以聚氯乙烯聚乙烯。聚丙烯的应用占主流，工程塑料类虽然有优异的耐腐性能，但因其价格的原因，在中等的腐蚀环境中首选的仍是价廉易得、加工容易的材料，工程塑料中尤以氟树脂应用面最广，增长也最快，热固性树脂大多...
【技术保护点】
1.一种耐腐蚀高分子材料，其特征在于，由以下重量份的组分制成：聚芳醚树脂：50‑80份；聚丁烯：10‑20份；PET：5‑20份；四氧化三铁：5‑10份；三氧化二铁：1‑5份；氧化铜：1‑5份；氧化镁：1‑5份；所述四氧化三铁、三氧化二铁、氧化铜、氧化镁的目数为800‑2000目。
【技术特征摘要】
1.一种耐腐蚀高分子材料，其特征在于，由以下重量份的组分制成：聚芳醚树脂：50-80份；聚丁烯：10-20份；PET：5-20份；四氧化三铁：5-10份；三氧化二铁：1-5份；氧化铜：1-5份；氧化镁：1-5份；所述四氧化三铁、三氧化二铁、氧化铜、氧化镁的目数为800-2000目。2.根据权利要求1所述的一种耐腐蚀高分子材料，其特征在于，由以下重量份的组分制成：聚芳醚树脂：60-70份；聚丁烯：10-15份；...
【专利技术属性】
技术研发人员：张祖森，
申请(专利权)人：天津中硕高分子材料有限公司，
类型：发明
国别省市：天津,12
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。