The invention discloses a thermoplastic composite material for laser direct forming technology and its preparation method, which consists of the following raw materials: liquid crystal polyester 59%98.9%, laser sensitive additive 1%10%, compatibilizer 0.1%1%, filler 0%30%. Laser sensitive additives and compatibilizers were pre-mixed and then extruded with other raw materials after vacuum heat treatment for 2 to 6 hours. The thermoplastic composite material of the invention improves the dispersibility and activation ability of the laser sensitive additive, reduces the dosage, and maintains the characteristics of high temperature resistance and high toughness of liquid crystal polyester, so the composite material has excellent comprehensive performance.
【技术实现步骤摘要】
一种用于激光直接成型技术的热塑性复合材料及其制备方法
本专利技术涉及一种热塑性复合材料，具体为一种用于激光直接成型技术的液晶聚合物复合材料，以及这种复合材料的制备方法，属液晶聚合物复合材料
技术介绍
激光直接成型(LDS，LaserDirectStructuring)技术是一种激光加工与化学镀制程的生产技术，用以制作三维模塑互联器件(3D-MID，Three-dimensionalMouldedInterconnectDevice)。其原理是将激光照射到含有激光敏感添加剂的塑胶制件上，活化出电路图案，该制件上被活化的区域可以在无电化学镀中沉积铜、镍、金等金属，从而赋予三维塑胶制件导电功能。如今，电子元件变得日益流行并且通常提供无线通信能力。例如，电子元件可以使用815MHz～3600MHz下的移动电话频段(2G/3G/4G制式)进行通信。电子元件也可以使用2.4GHz和5GHz频带(802.11a/b/g/n/ac)的无线网络进行通信。这样的电子元件结构体，即3D-MID，通常为塑胶基材及其上形成的导电元件或通道构成，是一种具有集成印刷导体或电路版图的三...
【技术保护点】
1.一种用于激光直接成型技术的热塑性复合材料，其特征在于：由以下重量百分比计的原料组成：
【技术特征摘要】
1.一种用于激光直接成型技术的热塑性复合材料，其特征在于：由以下重量百分比计的原料组成：2.根据权利要求1所述的一种用于激光直接成型技术的热塑性复合材料，其特征在于：所述热致性液晶聚酯为使用芳香族化合物作为原料单体制备而成的液晶聚酯。3.根据权利要求1所述的一种用于激光直接成型技术的热塑性复合材料，其特征在于：所述的激光敏感添加剂为锡和锑的混杂金属氧化物。4.根据权利要求1所述的一种用于激光直接成型技术的热塑性复合材料，其特征在于：所述的相容剂为硬脂酸盐类，包括硬脂酸钠、硬脂酸钙、硬脂酸锂中的一种或几种的组合。5.根据权利要求1所述的一种用于激光直接成型技术的热塑性复合材料，其特征在于：所述的填料为磨碎玻璃纤维、滑石、...
【专利技术属性】
技术研发人员：许斌，高波，周文，
申请(专利权)人：上海普利特化工新材料有限公司，上海普利特复合材料股份有限公司，浙江普利特新材料有限公司，重庆普利特新材料有限公司，上海普利特材料科技有限公司，
类型：发明
国别省市：上海,31
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。