The invention relates to a composite polymer materials, specifically, polymer composite materials of the invention comprises the following components by weight: 50 to 80 portions of butyl rubber, styrene butadiene rubber, nitrile rubber 5 ~ 10 5 ~ 10, three ~ 8 5 butyl tin chloride, melamine 3 ~ 5 from 4 to 6, magnesium phosphate, liquid paraffin 2 to 5 copies, two methyl silicone oil 0.1 - 0.5 and 1 to 5 portions of zinc stearate. The invention of the polymer composite materials for energy saving and environmental protection, high mechanical strength, high temperature resistance, thermal insulation effect is good, in the production process does not add any harmful ingredients, the non-toxic, clean effect, simple preparation method and is suitable for industrial production.
【技术实现步骤摘要】
一种复合高分子材料
本专利技术属于功能材料领域,涉及一种复合高分子材料。
技术介绍
传统保温隔热材料是以降低导热系数和传导系数为主,而市场上现有的国产保温隔热涂料存在功能单一、效果有限及有效期短等问题,难以广泛应用,进口复合涂料效果虽好,但价格偏高,相应增加了生产成本,不利于大规模应用。
技术实现思路
针对上述情况,本专利技术的目的在于提供一种复合高分子材料。为了实现上述目的,本专利技术采用以下技术方案:一种复合高分子材料,其包含以重量份数计的下列组分:丁基橡胶50~80份、丁苯橡胶5~10份、丁腈橡胶5~10份、氯化三丁基锡5~8份、密胺3~5份、磷酸镁4~6份、液体石蜡2~5份、二甲基硅油0.1~0.5份和硬脂酸锌1~5份。优选的,上述复合高分子材料包含以重量份数计的下列组分:丁基橡胶60~70份、丁苯橡胶6~9份、丁腈橡胶6~9份、氯化三丁基锡6~7份、密胺3.5~4.5份、磷酸镁4.5~5.5份、液体石蜡3~4份、二甲基硅油0.2~0.4份和硬脂酸锌2~4份。更优选的,上述复合高分子材料包含以重量份数计的下列组分:丁基橡胶65份、丁苯橡胶8份、丁腈橡胶8份、氯化三丁基锡6份、密胺4份、磷酸镁5份、液体石蜡4份、二甲基硅油0.3份和硬脂酸锌3份。优选的,在上述复合高分子材料中,所述丁基橡胶中异戊二烯的摩尔含量为1~5%。优选的,在上述复合高分子材料中,所述丁苯橡胶中苯乙烯的摩尔含量为20~40%。优选的,在上述复合高分子材料中,所述丁腈橡胶中苯乙烯的摩尔含量为20~40%。与现有技术相比,本专利技术的复合高分子材料节能环保、机械强度高、耐高温、保温隔温效 ...
【技术保护点】
一种复合高分子材料,其包含以重量份数计的下列组分:丁基橡胶50~80份、丁苯橡胶5~10份、丁腈橡胶5~10份、氯化三丁基锡5~8份、密胺3~5份、磷酸镁4~6份、液体石蜡2~5份、二甲基硅油0.1~0.5份和硬脂酸锌1~5份。
【技术特征摘要】
1.一种复合高分子材料,其包含以重量份数计的下列组分:丁基橡胶50~80份、丁苯橡胶5~10份、丁腈橡胶5~10份、氯化三丁基锡5~8份、密胺3~5份、磷酸镁4~6份、液体石蜡2~5份、二甲基硅油0.1~0.5份和硬脂酸锌1~5份。2.根据权利要求1所述的复合高分子材料,其特征在于,所述复合高分子材料包含以重量份数计的下列组分:丁基橡胶60~70份、丁苯橡胶6~9份、丁腈橡胶6~9份、氯化三丁基锡6~7份、密胺3.5~4.5份、磷酸镁4.5~5.5份、液体石蜡3~4份、二甲基硅油0.2~0.4份和硬脂酸锌2~4份。3.根据权利要求2...
【专利技术属性】
技术研发人员:周春毅,
申请(专利权)人:吴中区穹窿山天仲高分子材料技术研究所,
类型:发明
国别省市:江苏,32