The invention relates to the field of chemical technology, in particular to a modified benzotriazole and a preparation method thereof. The mixture of benzotriazole or methyl benzotriazole, diethanolamine, formaldehyde solution, solvent and water-carrying agent was stirred and refluxed, separated, and then the substrates were distilled under vacuum to evaporate the remaining water and solvent, which resulted in a yellowish slightly viscous liquid. Modified benzotriazole has higher solubility in water, and has better corrosion inhibition performance for copper and carbon steel, so as to improve the corrosion resistance. The solubility of benzotriazole in ultra-pure water is 120% higher than that before modification. The initial decomposition temperature of benzotriazole is above 250 C. The thermal stability of modified benzotriazole is good.
【技术实现步骤摘要】
一种改性苯并三氮唑及其制备方法
本专利技术涉及属于化学
,特别涉及一种改性苯并三氮唑及其制备方法。
技术介绍
苯并三氮唑因其分子中有苯环和电负性较大的3个N原子,存在提供π电子的共轭体系和孤对电子。金属铜等表面的原子易于取代苯并三氮唑中—NH中的H原子形成共价键,而另一苯并三氮唑分子中N原子提供孤对电子与Cu原子的空轨道形成配位键,因而有效抑制了铜的腐蚀速率。而苯并三氮唑中的共轭π键也可降低铜腐蚀率。但是,由于苯并三氮唑自身在水性和油性溶液的溶解度差。因此,苯并三氮唑作为铜腐蚀缓蚀剂使用受到了极大的限制。
技术实现思路
本专利技术要解决的是苯并三氮唑在水溶液中的溶解度差问题,提供一种对苯并三氮唑进行改性的新方法。一种改性苯并三氮唑,将苯并三氮唑或甲基苯并三氮唑、二乙醇胺、甲醛溶液、溶剂按照比例依次加入三口烧瓶中,向其中加入的带水剂,在90-100℃下,混合搅拌回流反应3-5h,分离出溶剂水和产生的水;将上述底物进行减压蒸馏,蒸出剩余水和溶剂,即得到淡黄色略黏稠液体;其中,苯并三氮唑或甲基苯并三氮唑、二乙醇胺、甲醛溶液摩尔比1.0-1.2:1.0:1.0,带水剂占 ...
【技术保护点】
1.一种改性苯并三氮唑,其特征在于:将苯并三氮唑或甲基苯并三氮唑、二乙醇胺、甲醛溶液、溶剂按照比例依次加入三口烧瓶中,向其中加入的带水剂,在90‑100℃下,混合搅拌回流反应3‑5h,分离出溶剂水和产生的水;将上述底物进行减压蒸馏,蒸出剩余水和溶剂,即得到淡黄色略黏稠液体;其中,苯并三氮唑或甲基苯并三氮唑、二乙醇胺、甲醛溶液摩尔比1.0‑1.2:1.0:1.0,带水剂占总体积的20%~30%。
【技术特征摘要】
1.一种改性苯并三氮唑,其特征在于:将苯并三氮唑或甲基苯并三氮唑、二乙醇胺、甲醛溶液、溶剂按照比例依次加入三口烧瓶中,向其中加入的带水剂,在90-100℃下,混合搅拌回流反应3-5h,分离出溶剂水和产生的水;将上述底物进行减压蒸馏,蒸出剩余水和溶剂,即得到淡黄色略黏稠液体;其中,苯并三氮唑或甲基苯并三氮唑、二乙醇胺、甲醛溶液摩尔比1.0-1.2:1.0:1.0,带水剂占总体积的20%~30%。2.根据权利要求1所述改性苯并三氮唑,其特征在于:所述带水剂为二甲苯。3.根据权利要求1所述改性苯并三氮唑,其特征在于:所述溶剂为甲苯。4.根据权利要求1所述改性苯并三氮唑,其特征在于:所述所述...
【专利技术属性】
技术研发人员:王绍勤,李胜男,辛明昊,张海菊,葛登文,吴迪,郭坤,杨洋,
申请(专利权)人:盘锦辽河油田大力集团有限公司,
类型:发明
国别省市:辽宁,21