一种用于电机定子绕组的浸渍树脂，由以下重量份数的原料组成：环氧树脂30～50份、有机纤维3～5份、碳纤维4～6份、耐高温材料1～5份、阻聚剂0.05～0.07份。本发明专利技术的有益效果为：本发明专利技术中使用的为耐高温的环氧树脂原料以及其他辅助原料均具有良好的耐高温性，耐高温材料的加入大大提高了整个浸渍树脂的耐高温性；该发明专利技术所述的浸渍树脂具有良好的介电性及耐腐蚀性能，还具有较高的机械强度。

An impregnating resin for motor stator winding

An impregnating resin for motor stator winding consists of 30-50 parts epoxy resin, 3-5 parts organic fiber, 4-6 parts carbon fiber, 1-5 parts high temperature resistant material and 0.05-0.07 parts polymer inhibitor. The beneficial effects of the invention are as follows: the epoxy resin material used in the invention for high temperature resistance and other auxiliary materials have good high temperature resistance, the addition of high temperature resistant materials greatly improves the high temperature resistance of the whole impregnated resin; the impregnated resin has good dielectric and corrosion resistance, and also has high mechanical strength.

【技术实现步骤摘要】
一种用于电机定子绕组的浸渍树脂
本专利技术属于定子绕组浸渍领域，具体涉及一种用于电机定子绕组的浸渍树脂。
技术介绍
根据线圈绕制的形状与嵌装布线方式不同，可分为集中式和分布式两类。集中式绕组的绕制和嵌装比较简单，但效率较低，运行性能也差。目前的交流电动机定子绝大部分都是应用分布式绕组，根据不同机种、型号及线圈嵌绕的工艺条件，电动机各自设计采用不同的绕组型式和规格，故其绕组的技术参数也不相同。为了提高电机的机械强度、绝缘性能以及导热性能，传统的电机定子的制作工艺一般是在嵌线完成之后，再用绝缘漆加以浸渍、固化。若绝缘漆的导热系数小，定子的整体导热效果就不好，导致电机运行时产生的热量不能及时散出去，运行的时间长了就会把电机烧毁；同时浸渍树脂不仅具有良好的耐高温性，还必须具有良好的机械强度、介电性。
技术实现思路
本专利技术所要解决的技术问题在于：现有绝缘漆的导热系数小，定子的整体导热效果就不好，导致电机运行时产生的热量不能及时散出去，运行的时间长了就会把电机烧毁。为此，提供一种用于电机定子绕组的浸渍树脂。为解决上述技术问题，本专利技术的技术方案为：一种用于电机定子绕组的浸渍树脂，由以下重量份数本文档来自技高网...

【技术保护点】
1.一种用于电机定子绕组的浸渍树脂，其特征在于：由以下重量份数的原料组成：环氧树脂30～50份、有机纤维3～5份、碳纤维4～6份、耐高温材料1～5份、阻聚剂0.05～0.07份。

【技术特征摘要】
1.一种用于电机定子绕组的浸渍树脂，其特征在于：由以下重量份数的原料组成：环氧树脂30～50份、有机纤维3～5份、碳纤维4～6份、耐高温材料1～5份、阻聚剂0.05～0.07份。2.根据权利要求1所述的一种用于电机定子绕组的浸渍树脂，其特征在于：由以下重量份数的原料组成：环氧树脂30份、有机纤维3份、碳纤维4份、耐高温材料1份、阻聚剂0.05份。3.根据权利要求1所述的一种用于电机定子绕组的浸渍树脂，其特征在于：由以下重量份数的原料组成：环氧树脂50份、有机纤维5份、碳纤维6份、耐高温材料5份、阻聚剂0.07份。4.根据权利要求1所述的一种用于电机定子绕组的浸渍树脂，其...