A Pre-hardening plastic die steel and its preparation method are described. Its components are C 0.32-0.40%, Si 0.20-0.35%, Mn 1.30-1.60%, Cr 1.80-2.10%, Ni 0.90-1.15%, P < 0.015%, S < 0.005%, V 0.10-0.35%, and the remainder is Fe. Its isotropy is more than 0.80. The methods are: (1) smelting molten steel and casting into ingots; (2) heating to 1200-1250 degrees after preheating at 600-700 degrees centigrade; (3) cooling with furnace after forging; (4) normalizing at 880+10 degrees centigrade; (5) holding at 900-940 degrees centigrade for 2-3 hours, then water cooling; (6) tempering at 450-550 degrees centigrade. The pre-hardened plastic die steel prepared by the method of the invention greatly improves the hardenability and the transverse impact toughness.
【技术实现步骤摘要】
一种预硬型塑料模具钢及其制备方法
本专利技术属于冶金材料
，特别涉及一种预硬型塑料模具钢及其制备方法。
技术介绍
塑料模具作为塑料成型工业的重要工艺装备，随着汽车产业及家电行业的高速发展，对塑料模具钢性能上的要求也越来越严格；模具材料也由低级的碳素工具钢向合金工具钢发展，目前塑料模具钢使用量最大的，是由美国提出的P20系列预硬型塑料模具钢；对应我国国标为3Cr2Mo钢，其工作温度为250℃左右，服役期间受到高压和腐蚀作用，脱模时存在摩擦磨损现象；目前3Cr2Mo钢存在淬透性不足，调质处理后硬度不足导致耐磨性较差及横向冲击韧性较低的缺点，无法满足现在对高品质模具钢的要求。
技术实现思路
为了解决上述技术问题，本专利技术提供一种预硬型塑料模具钢及其制备方法，通过添加少量的V元素来替代Mo元素，细化晶粒并提升耐磨性，提高Mn元素含量的同时加入Ni元素，增大塑料模具钢的淬透性，适当降低Si元素含量来降低回火脆性，提升横向冲击韧性。本专利技术的预硬型塑料模具钢的成分按质量百分比含C0.32～0.40％，Si0.20～0.35％，Mn1.30～1.60％，Cr1.80～2....
【技术保护点】
1.一种预硬型塑料模具钢，其特征在于成分按质量百分比含C 0.32～0.40％，Si 0.20～0.35％，Mn 1.30～1.60％，Cr 1.80～2.10％，Ni 0.90～1.15％，P≤0.015％，S≤0.005％，V 0.10～0.35％，余量为Fe；其等向性≥0.80。
【技术特征摘要】
1.一种预硬型塑料模具钢，其特征在于成分按质量百分比含C0.32～0.40％，Si0.20～0.35％，Mn1.30～1.60％，Cr1.80～2.10％，Ni0.90～1.15％，P≤0.015％，S≤0.005％，V0.10～0.35％，余量为Fe；其等向性≥0.80。2.根据权利要求1所述的一种预硬型塑料模具钢，其特征在于其组织为回火马氏体。3.一种预硬型塑料模具钢的制备方法，其特征在于包括以下步骤：(1)冶炼：采用真空感应冶炼的方式冶炼钢水，然后浇铸制成圆柱形的钢锭，其成分按质量百分比含C0.32～0.40％，Si0.20～0.35％，Mn1.30～1.60％，Cr1.80～2.10％，Ni0.90～1.15％，P≤0.015％，S≤0.005％，V0.10～0.35％，余量为Fe；(2)锻前加热：将钢锭加热至600～700℃预热3～4h，然后加热至1200～125...
【专利技术属性】
技术研发人员：李长生，任津毅，韩亚辉，贺帅，邱春林，高彩茹，
申请(专利权)人：东北大学，
类型：发明
国别省市：辽宁,21