The invention discloses a high strength printing base film and a preparation method thereof, which relates to the technical field of decorative plates. The invention consists of 60 to 80 parts of PVC resin, 10 to 15 parts of EVA, 5 to 10 parts of organotin stabilizer, 4 to 6 parts of MBS resin, 3 to 6 parts of internal lubricant, 4 to 6 parts of external lubricant and 2 to 4 parts of ACR additives. The coating liquid prepared by using SiO 2 and nano-alumina as raw materials can form an alloy layer composite structure on the printing base film, which significantly improves the printing performance. The tensile and flexural strength of the brush base film make it have excellent mechanical properties.
【技术实现步骤摘要】
高强度印刷基膜及其制备方法
：本专利技术涉及基膜
，具体涉及高强度印刷基膜及其制备方法。
技术介绍
：现有技术中，常见的地面装饰材料有瓷砖、木地板或地毯等，其原材料多来自天然，长期过度的开发自然资源，对生态环境造成的影响不可小视；随着人们生活水平的提高，地面装饰材料需求量随之增长，如何既能有效开发和综合利用自然资源，符合节能环保的基本准则，又能使地面装饰材料美观大方、经济实用、满足人们的不同使用目的并具有一定的舒适性，采用复合、合成等方式生产地面装饰材料已是大势所趋。PVC地板是当今世界上非常流行的一种新型轻体地面装饰材料，是一种在欧美及亚洲的日韩广受欢迎的产品，风靡国外，从80年代初开始进入中国市场，至今在国内的大中城市已经得到普遍的认可，使用非常广泛，可以运用在各种场所如家庭、医院、办公楼、工厂、超市等。PVC地板是指采用聚氯乙烯材料生产的地板，以聚氯乙烯及其共聚树脂为主要原料，加入填料、增塑剂、稳定剂、着色剂等辅料，在片状连续基材上，经涂敷工艺或经压延、挤出或挤压工艺生产而成，PVC地板及其衍生地板已经越来越受到广大消费者的喜爱，使用也越来越广泛，但目...
【技术保护点】
1.高强度印刷基膜，其特征在于，由以下质量份的原料组成：PVC树脂60‑80份、EVA 10‑15份、有机锡稳定剂5‑10份、MBS树脂4‑6份、内润滑剂3‑6份、外润滑剂4‑6份、ACR助剂2‑4份。
【技术特征摘要】
1.高强度印刷基膜，其特征在于，由以下质量份的原料组成：PVC树脂60-80份、EVA10-15份、有机锡稳定剂5-10份、MBS树脂4-6份、内润滑剂3-6份、外润滑剂4-6份、ACR助剂2-4份。2.一种如权利要求1所述的高强度印刷基膜的制备方法，其特征在于，包括以下步骤：(1)混料：称取上述各种原材料放入混合机中，进行低混到高混，待温度达到125℃，烘干水分，混合均匀，然后放入冷混机，冷却至40℃；(2)挤压塑化：将步骤(1)所得的混料输入行星挤出机内，在180℃的温度下，挤出塑化；(3)定型：将步骤(2)所得的塑化后的混料通过五辊压延成型，然后在温度为20℃的水里进行冷处理，得到基膜；(4)除尘：先人工清除基膜表面的杂质，然后使用吸尘器进一步去除灰尘，再经过两道静电除尘；(5)改性：用覆膜液进行覆膜，然后进行紫外线固化、烘干为成品，最后检验、分切、收卷、包装。3.根据权利要求2所述的高强度印刷基膜的制...
【专利技术属性】
技术研发人员：胡伟，吴磊，张德顺，李汪洋，陈辉，范守贵，王成爱，孙天龙，赵凯，
申请(专利权)人：安徽嘉阳新材料科技有限公司，
类型：发明
国别省市：安徽,34
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。