The invention provides a protective coating for cigarette box wire drawing line and a preparation method thereof. The coating comprises the following components: polyurethane modified acrylic resin 5%-25%; modified vinyl ester resin 4%-30%; ether cellulose resin 2%-6%; monomer 10%-20%; initiator 4%-8%; additive 1%-3%; solvent 40%-74%; \u3002 The coating provided by the invention has the following advantages: low volatile organic matter emission, less wet coating amount, high production efficiency and low cost; excellent adhesion fastness with polyester film and evaporated aluminium layer; wide process adaptability for preparing holographic rainbow effect, good hot pressing effect, non-stick plate and plug plate, etc.
【技术实现步骤摘要】
用于烟盒拉丝线的防护层涂料及其制备方法
本专利技术涉及涂料
，具体地，涉及一种用于烟盒拉丝线的防护层涂料及其制备方法；尤其是指一种紫外光固化后可热压出全息彩虹效果的防护层涂料。
技术介绍
全息彩虹效果的复合卡纸主要由卡纸、蒸镀的铝层、具有全息效果的防护涂层以及聚酯薄膜组成，因复合卡纸流平好、平整度佳、彩虹效果炫丽、识别性突出等优点，而被广泛用作高档烟盒的拉丝线。现用的烟盒拉丝线防护涂料为溶剂型双组份涂料，在挥发性有机物排放、附着牢度以及制备全息彩虹效果的热压工艺上都存在较大缺陷，严重限制了其在烟盒拉丝线上的应用。如公开号为CN103059698A的专利技术专利中公开了一种可紫外光固化的全息复合镀铝涂料组合物及其制备方法，该涂料组合物包括如下重量百分比含量的各组分：活性齐聚物15～36％，氯醋树脂3～20％，单体10～25％，光引发剂1～8％，助剂0.2～1.5％，溶剂30～60％；其中，活性齐聚物为满足烟标行业VOC要求的环氧丙烯酸树脂、聚酯丙烯酸树脂、聚氨酯丙烯酸树脂、纯丙烯酸树脂中的一种或者几种的混合物；氯醋树脂是分子量为1.5～6万的二元氯乙烯-醋酸乙...
【技术保护点】
1.一种用于烟盒拉丝线的防护层涂料，其特征在于，包括如下重量百分比含量的各组分：
【技术特征摘要】
1.一种用于烟盒拉丝线的防护层涂料，其特征在于，包括如下重量百分比含量的各组分：2.根据权利要求1所述的用于烟盒拉丝线的防护层涂料，其特征在于，所述聚氨酯改性丙烯酸树脂包括聚酯型聚氨酯改性丙烯酸树脂、聚醚型聚氨酯改性丙烯酸树脂中的一种或两种。3.根据权利要求1或2所述的用于烟盒拉丝线的防护层涂料，其特征在于，所述聚氨酯改性丙烯酸树脂的官能数为2～6官，黏度为在25℃下，4000～80000cps。4.根据权利要求1所述的用于烟盒拉丝线的防护层涂料，其特征在于，所述改性乙烯基酯树脂包括双酚A型环氧乙烯基树脂、酚醛环氧乙烯基树脂中的一种或两种；所述改性乙烯基酯树脂的重均分子量为10000～60000。5.根据权利要求1所述的用于烟盒拉丝线的防护层涂料，其特征在于，所述醚类纤维素树脂包括甲基纤维素树脂、乙基纤维素树脂、羧甲基纤维素树脂中的一种或几种；所述醚类纤维素树脂的重均分子量为5000～20000。6.根据权利要求1所述的用于烟盒拉丝线的防护层涂料，其特征在于，所述单体为含有2～4个烯属不饱和双键的丙烯酸酯中的一种或几种；所述单体的黏度为在25℃下...
【专利技术属性】
技术研发人员：虞明东，韩莲，
申请(专利权)人：上海乘鹰新材料有限公司，上海维凯光电新材料有限公司，
类型：发明
国别省市：上海,31
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。