The present invention provides a tri-azobenzene molecule and its preparation method. The target molecule is obtained by two-step reaction, that is, diazotization of 2,4,6 triaminophenol to obtain diazo salt, and then coupling with isophthalic acid to obtain tri-azobenzene molecule. Compared with other small azobenzene molecules, the energy value and half-life of azobenzene molecules have been greatly improved due to the large steric hindrance between molecules and the existence of hydrogen bonds between multiple molecules. In further research, it is planned to graft them onto graphene or polymer templates in order to further enhance the energy density, which is conducive to solar energy storage.
【技术实现步骤摘要】
三枝偶氮苯分子及其制备方法
本专利技术涉及功能材料领域，更具体地说涉及一种新型偶氮分子的设计及制备方法，其在可见光太阳能存储领域具有广泛的应用前景。
技术介绍
高效捕捉太阳能并把其循环转换为其他形式的能量(如电能，化学能，和热能)进行利用成为近年来的研究焦点。目前不同类型的太阳能电池(包含无机，有机，复合材料，具有金属氧化宽键的光催化类燃料系统)对于太阳热的收集和储存很大程度上依赖流体物质。比如水，空气，融熔盐和相转变材料。特别是，具有高相转变焓的材料在储存太阳能方面占据非常大的优势。另一种鲜有人知但是高度受欢迎的太阳能储能方法是:利用光致变色的分子转换和储存太阳能(以热的形式)。这种分子的特点是在光的照射下发生异构化，由稳定态转变为亚稳态，从而把能量储存在化学键中，当受到外界刺激比如光照或者加热时释放出热量，并且再次回复到稳定态。这类材料与其他太阳能装置以及相转变材料相比最独特的优势是能够实现离网式储能和释放能量。而且除此自外，这种材料由于制造简单，操作方便，在热释放可控的大尺寸和便携式器件方面可以对其进行深入研究。目前具有可逆的光致变色特点的分子主要有蒽，二苯...
【技术保护点】
1.三枝偶氮苯分子，其特征在于：具有三枝结构和形成多重氢键，其结构式如下：
【技术特征摘要】
1.三枝偶氮苯分子，其特征在于：具有三枝结构和形成多重氢键，其结构式如下：2.三枝偶氮苯分子的制备方法，其特征在于：按照下述步骤进行：步骤1，重氮化：将1，3，5-三氨基苯酚、浓盐酸以及亚硝酸钠置于反应容器中，在冰浴条件下反应20-60min，1，3，5-三氨基苯酚和浓盐酸以及亚硝酸钠的摩尔比为(1-2)：(6-8)：(3-4)，得到重氮盐溶液；步骤2，耦合：在无氧条件下，把步骤1制备得到的重氮盐溶液滴加到间苯二甲酸中，反应8-12h，其中，1，3，5-三氨基苯酚和间苯二甲酸的摩尔比是(1-2)：(2-4)，间苯二甲酸溶解在30ml的NaOH水溶液里，间苯二甲酸和NaOH的摩尔比是(1-2)：(1-3)，上述反应结束后，向反应体系中加入盐酸使其析出，水洗、分离、蒸馏和干燥后，得到三枝偶氮苯分子(AZO)。3.根据权利要求2所述的三枝偶氮苯分子的制备方法，其特征在于：在步骤1中，冰浴条件下反应20-40min。4.根据权利要求2所述的三枝偶氮苯分子的制备方法，其特征在于...
【专利技术属性】
技术研发人员：冯奕钰，符林霞，封伟，董立奇，
申请(专利权)人：天津大学，
类型：发明
国别省市：天津,12
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。