The invention discloses a rapid maintenance method for expansion joint of recycling vulcanized bed boiler feeder, which includes the following steps: S1, a set of rectangular holes are arranged along the expansion joint of the feeder, and the rectangular holes are distributed along the circumference of the feeder tube; the rectangular holes are 50cm long and 30cm wide; S2, the castable burned in the expansion joint is removed through the rectangular holes; S3, measuring the inner diameter of the expansion joint, making the same as the inner diameter. The corresponding pouring formwork fixes the pouring formwork on the inner diameter of the expansion joint; S4, pouring through castables in the expansion joint; S5, drying castables; the overhaul device includes a rectangular hole arranged above the expansion joint of the returner, which is used to remove burned castables, install the pouring formwork and serve as a pouring passage; the method and the device can quickly pour the expansion joint of the returner. Inspection, safe and fast.
【技术实现步骤摘要】
一种循环硫化床锅炉返料器膨胀节快速检修方法及装置
本专利技术涉及一种循环硫化床锅炉返料器膨胀节快速检修方法及装置。
技术介绍
随着越来越多的循环硫化床锅炉的投用，在运行一段时间后，返料器膨胀节内部浇注料会出现开裂、脱落现象，严重影响到锅炉的安全稳定运行。一旦膨胀节内部浇注料脱落，如不及时修复，会造成膨胀节烧坏，漏高温返料灰，严重的导致被迫停炉或发生安全事故。近几年来，我公司4台循环硫化床锅炉，自投用以来，先后不同程度出现膨胀节，回料管浇注料脱落现象，造成高温返料灰泄漏，运行现场环境，也出现过返料器膨胀节被烧毁、报废情况。当膨胀节及回料管内浇注料脱落后，如果不及时处理，膨胀节就会被烧坏。其检修方法一是在浇注料脱落部位外侧，用铁板焊围子，然后在围子里倒入浇注料，这种方法简单快捷，但会造成膨胀节和料腿，彻底报废，如果停下来检修，需要很长时间，因其内部结构，停炉后降温特别缓慢，如强制降温，将会导致返料器内部浇注料开裂变形。正常情况下，返料器降温大约需要一周左右时间，在内部作业，需要将损坏的浇注料全部清除，然后在内部支模，再用浇注料重新浇筑，返料器内部空间特别小，在受限空间...
【技术保护点】
1.一种循环硫化床锅炉返料器膨胀节快速检修方法，其特征在于，包括以下步骤：S1、在返料器膨胀节上方，沿返料管设置一组矩形孔，矩形孔沿返料管圆周分布；矩形孔长50cm、宽30cm；S2、通过矩形孔清除膨胀节内烧毁的浇注料；S3、测量膨胀节内径，制作与内径相适应的浇注模板，将浇注模板固定于膨胀节内径；S4、在膨胀节内通过浇注料进行浇注；S5、烘干浇注料。
【技术特征摘要】
1.一种循环硫化床锅炉返料器膨胀节快速检修方法，其特征在于，包括以下步骤：S1、在返料器膨胀节上方，沿返料管设置一组矩形孔，矩形孔沿返料管圆周分布；矩形孔长50cm、宽30cm；S2、通过矩形孔清除膨胀节内烧毁的浇注料；S3、测量膨胀节内径，制作与内径相适应的浇注模板，将浇注模板固定于膨胀节内径...
【专利技术属性】
技术研发人员：孙彩军，王如年，刘云行，
申请(专利权)人：安徽金禾实业股份有限公司，
类型：发明