In order to improve the hardness and wear resistance of WC Co cemented carbide, a plate-like crystal cemented carbide prepared by W Co C was prepared. The addition of nano-W powder can help to inhibit the growth of grains in sintering process, increase sintering temperature and prolong sintering time, and also produce cemented carbide samples with higher densification degree. The WC_Co cemented carbide with the best properties can be successfully prepared by combining several optimal process parameters. The hardness, densification degree and flexural strength of plate-like cemented carbide prepared by W Co C have been greatly improved. The invention can provide a new production process for preparing high-performance plate-like crystal cemented carbide.
【技术实现步骤摘要】
一种W-Co-C制备板状晶硬质合金所属
本专利技术涉及一种硬质合金材料，尤其涉及一种W-Co-C制备板状晶硬质合金。
技术介绍
WC-Co硬质合金是由一种或多种高硬度、高模量的间隙化合物与过渡族金属或其合金组成的复合材料，以其硬度高、红硬性高、抗压强度高、耐磨性好，耐蚀性与抗氧化性良好等性能广泛应用于切削刀具、矿用工具、模具、量具、耐磨零件以及机械密封等工业领域，被称为“现代工业的牙齿”。硬度、耐磨性及强度既是作为衡量WC-Co硬质合金好坏的重要技术指标，也是WC-Co硬质合金优于其他材料的根本。因此，提升WC-Co硬质合金的硬度、强度和耐磨性成为了WC-Co硬质合金研究领域的重中之重。含板状WC晶粒硬质合金的制备通常是利用具有板状形貌的W粉和石墨为原料化学合成板状WC晶粒或通过添加其他物质(如TiC，Y2O3，板状WC晶种等)诱导WC晶粒向板状发展等，但普遍存在着板状WC的数量和尺寸难以控制、板状晶粒比例少、成本高等缺点。
技术实现思路
本专利技术的目的是为了改善WC-Co硬质合金的硬度、耐磨性，设计了一种W-Co-C制备板状晶硬质合金。本专利技术解决其技术问题所采...
【技术保护点】
1.一种W‑Co‑C制备板状晶硬质合金的制备原料包括：高度扁平化程度的薄板状W粉。
【技术特征摘要】
1.一种W-Co-C制备板状晶硬质合金的制备原料包括：高度扁平化程度的薄板状W粉。2.根据权利要求1所述的W-Co-C制备板状晶硬质合金，其特征是W-Co-C制备板状晶硬质合金的制备步骤为：将原始粉末按实验设计方案称重、配料，配好后倒入管式炉中进行氢还原反应，制取中颗粒W粉，然后将制得的中颗粒W粉放入硬质合金球磨罐中进行湿磨，球磨介质为直径10mm的硬质合金球，球磨机转速为90r/min，球料比为12：1，球磨时间为24h，球磨结束后，将制得的粒料进行真空干燥，干燥时间为50min，干燥温度为40℃，随后加入5.0%的石蜡作为成形剂进行制粒，将制好的粉末加至单柱液压机中进行压制成形，将制好的压坯置于通氢钼丝炉中进行烧结，烧结温度为1460℃，保温时间为90min。3.根据权利要求1所述的W...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。