The invention relates to a flexible ceramic membrane, a preparation method and application thereof, belonging to the field of environmental protection water treatment technology. The flexible ceramic membrane is prepared from the following raw materials: 5%-10% ceramic membrane particles and 90%-95% PTFE particles. The flexible ceramic membrane enhances the pressure-bearing capacity and chemical stability of the membrane material, and also improves the anti-pollution ability of the membrane material due to the good hydrophilicity of the ceramic material, which makes the flexible ceramic membrane not only have the flexibility of the organic membrane material, but also have the rigidity and compressive capacity of the inorganic ceramic membrane.
【技术实现步骤摘要】
柔性陶瓷膜及其制备方法和应用
本专利技术涉及环保水处理
，特别是涉及一种柔性陶瓷膜及其制备方法和应用。
技术介绍
在环保行业中进行水处理，通常采用有机膜材料进行过滤，但是在应用的过程中，经常由于传统有机膜承压能力较差，出现在高压下容易压扁变形且不易恢复的问题；并且传统有机膜的抗污能力弱，膜容易被堵塞；使用寿命短且不耐高温。因此，也有采用无机陶瓷膜进行水过滤的方案，而无机陶瓷膜又存在脆性大，容易碎裂的问题，并且陶瓷膜的化学性质不稳定，容易与硅反应，导致膜孔被堵塞；造价成本高。
技术实现思路
基于此，有必要针对上述问题，提供一种柔性陶瓷膜及其制备方法和应用，该柔性陶瓷膜能保持良好的柔性，同时拥有很高的强度和韧性，在高压下膜丝都不会被压扁变形；具有良好的亲水性，能延缓膜污堵，延长使用寿命；并具有耐酸、耐碱、耐高温的稳定的化学性质，常温下不与任何物质发生反应；具成本低，通量大，能耗低的优点。一种柔性陶瓷膜，由以下重量百分比的原料制备而成：陶瓷膜颗粒5％-10％聚四氟乙烯颗粒90％-95％。上述柔性陶瓷膜通过将聚四氟乙烯颗粒包括在陶瓷膜颗粒周围，形成一定纳米级球状的复合材...
【技术保护点】
1.一种柔性陶瓷膜，其特征在于，由以下重量百分比的原料制备而成：陶瓷膜颗粒 5％‑10％聚四氟乙烯颗粒 90％‑95％。
【技术特征摘要】
1.一种柔性陶瓷膜，其特征在于，由以下重量百分比的原料制备而成：陶瓷膜颗粒5％-10％聚四氟乙烯颗粒90％-95％。2.根据权利要求1所述的柔性陶瓷膜，其特征在于，所述聚四氟乙烯颗粒的粒径为0.2-0.5μm，所述陶瓷膜颗粒的粒径为所述聚四氟乙烯颗粒粒径的5-100倍。3.根据权利要求1或2所述的柔性陶瓷膜，其特征在于，所述陶瓷膜颗粒选自：二氧化钛、刚玉、氧化铝、碳化硅中的至少一种。4.权利要求1-3任一项所述的柔性陶瓷膜的制备方法，其特征在于，包括以下步骤：混料：取陶瓷膜颗粒和聚四氟乙烯颗粒，加入助溶剂，加热搅拌使聚四氟乙烯包裹于陶瓷膜颗粒周围，形成复合膜材料；制料：将上述复合膜材料置于棒槽中充分搅拌后制成中空的管状棒料；成型：将上述管状棒料利用挤塑机挤出成型为中空薄型管状材料；脱除：在烘箱中加热脱除助溶剂；拉伸定型：将上述中空薄型管状材料在烘箱中加热拉伸定型，即得。5.根据权利要求4所述的柔性陶瓷膜...