The invention belongs to the field of flocculants, and specifically relates to a composite flocculant, which comprises the following components by weight: red clay 55 65, hydroxymethyl starch sodium 15 20, polyferric sulfate 5 10, polyacrylamide 2 6, grape polyphenol 1 2 and ferric sulfate 10 20. The invention has the following beneficial effects: 1. The invention creatively compounds red clay, sodium hydroxymethyl starch, polyferric sulfate, polyacrylamide and grape polyphenol to form a composite flocculant. When the mixed flocculant prepared by the invention is used for sewage treatment, the water content of the sludge after flocculation is as low as 60.7%, which greatly reduces the volume of the sludge and reduces the follow-up. Processing cost of process.
【技术实现步骤摘要】
一种复合絮凝剂及其制备方法
本专利技术属于絮凝剂领域，具体涉及一种复合絮凝剂及其制备方法。
技术介绍
随着城市化和工业化进程的加快，城镇化速率的急剧加快，导致了城市用水量逐步增加，随之而来的城市污水处理量也极大增加，污泥量也随之增加，而污泥脱水前常用的方法就是絮凝沉淀。目前使用的絮凝剂有天然絮凝剂和聚合絮凝剂，无论天然絮凝剂，还是聚合絮凝剂，其絮凝时间均较长、浊度均较高，絮凝完成后污泥的含水率都较高。
技术实现思路
为了解决上述问题，本专利技术提供一种复合絮凝剂及其制备方法，通过本专利技术的方法制备的絮凝剂絮凝时间短，浊度低，絮凝完成后污泥的含水率低。本专利技术提供了如下技术方案：一种复合絮凝剂，按照重量份计包括以下组份，红黏土55-65份、羟甲基淀粉钠15-20份、聚合硫酸铁5-10份、聚丙烯酰胺2-6份、葡多酚1-2份和硫酸铁10-20份。优选的，按照重量份计包括以下组份，红黏土55份，羟甲基淀粉钠18份、聚合硫酸铁7份、聚丙烯酰胺5份、葡多酚1份和硫酸铁15份。本专利技术还提供了一种复合絮凝剂的制备方法，包括如下步骤：S1、将羟甲基淀粉钠、红黏土和硫酸铁按照上述...
【技术保护点】
1.一种复合絮凝剂，其特征在于，按照重量份计包括以下组份，红黏土55‑65份、羟甲基淀粉钠15‑20份、聚合硫酸铁5‑10份、聚丙烯酰胺2‑6份、葡多酚1‑2份和硫酸铁10‑20份。
【技术特征摘要】
1.一种复合絮凝剂，其特征在于，按照重量份计包括以下组份，红黏土55-65份、羟甲基淀粉钠15-20份、聚合硫酸铁5-10份、聚丙烯酰胺2-6份、葡多酚1-2份和硫酸铁10-20份。2.根据权利要求1所述的一种复合絮凝剂，其特征在于，按照重量份计包括以下组份，红黏土55份，羟甲基淀粉钠18份、聚合硫酸铁7份、聚丙烯酰胺5份、葡多酚1份和硫酸铁15份。3.一种根据权利要求1或2所述复合絮凝剂的制备方法，其特征在于，包括如下步骤：S1、将羟甲基淀粉钠、红黏土和硫酸铁按照上述份数关系依次加入水中，然后将溶液的pH调节至中性，在20-40℃中反应1-2h；S2、将葡多酚、聚合硫酸铁、聚丙烯酰胺按照上述份数关系混合均匀后，加入S1的反应液中，均匀搅拌反应1-2h，放入100-120℃...
【专利技术属性】
技术研发人员：宋永莲，章长江，杨奎，黄健，张华，
申请(专利权)人：安徽中环环保科技股份有限公司，安徽建筑大学，
类型：发明
国别省市：安徽,34