The invention belongs to the technical field of photocatalyst, in particular to a bismuth photocatalyst and its preparation method and application. The bismuth photocatalyst provided by the invention comprises bismuth molybdate and Cetyltrimethylammonium Bromide in chemical composition. The bismuth molybdate is lamellar and forms an embroidered spherical structure by intermolecular force connection; the cetyltrimethylammonium bromide is adsorbed on the surface of lamellar bismuth molybdate by bromide ion; the bismuth photocatalyst has pore. The catalyst provided by the invention has excellent catalytic performance. In the photocatalytic reduction of carbon dioxide reaction, methanol production can reach 30.4-106.5 um ol gcatal after 4 hours of reaction.
【技术实现步骤摘要】
一种铋系光催化剂及其制备方法和应用
本专利技术属于光催化剂
，具体涉及一种铋系光催化剂及其制备方法和应用。
技术介绍
近年来，超薄的二维层状半导体材料在光催化剂领域引起了广泛关注，如：g-C3N4，过渡金属二硫化物等，主要原因是超薄的二维层状材料，有利于光生载流子从材料内部迁移到材料表面，可以大大减小电子空穴对的复合率，改善光催化活性。另外，研究表明，费米能级附近的光生载流子的空间分布主要集中在材料的表面，这就意味着有活性光生电子空穴对主要来源于材料的表面。将半导体催化剂制备成超薄层状的材料可以大大增加比表面积，从而增加活性的光生载流子在材料表面的数目。因此，将不同的半导体催化剂制备成单层或者较薄的二维层状材料是改善其光催化性能的有效方式。近年来铋系化合物由于其禁带宽度较窄，符合在可见光区域的响应条件、稳定、无毒等优势而引起广大研究者的兴趣。将铋系多元氧化物制备成超薄层状纳米片是改善其光催化性能的有效途径之一，因此在近几年的研究中，报道出了多种单层Bi系多元氧化物在光催化领域的应用。目前制备的单层铋系多元氧化物具有较好的催化活性，但用于光催化二氧化碳还原反应...
【技术保护点】
1.一种铋系光催化剂，化学组成上包括钼酸铋和十六烷基三甲基溴化铵，所述钼酸铋为片层状，通过分子间作用力连接形成绣球状结构；所述十六烷基三甲基溴化铵通过溴离子吸附在片层状钼酸铋的表面；所述铋系光催化剂具有孔隙。
【技术特征摘要】
1.一种铋系光催化剂，化学组成上包括钼酸铋和十六烷基三甲基溴化铵，所述钼酸铋为片层状，通过分子间作用力连接形成绣球状结构；所述十六烷基三甲基溴化铵通过溴离子吸附在片层状钼酸铋的表面；所述铋系光催化剂具有孔隙。2.如权利要求1所述的铋系光催化剂，其特征在于，所述孔隙的容积＞0.14cm3·g-1；所述铋系光催化剂的比表面积＞41m2·g-1；所述铋系光催化剂的平均直径为3～4μm。3.权利要求1或2所述铋系光催化剂的制备方法，包括以下步骤：提供包括铋源、钼源、十六烷基三甲基溴化铵和乙二醇的反应料液；对所述反应料液进行加热，经自组装得到铋系光催化剂。4.如权利要求3所述的制备方法，其特征在于，所述反应料液中，铋源中铋离子与钼源中钼酸根离子的摩尔比为2:1。5.如权利要求3或4所述的制备方法，其特征在于，所述反应...
【专利技术属性】
技术研发人员：代威力，马增鋆，王腾瑶，罗胜联，余俊杰，罗旭彪，杨丽霞，涂新满，邹建平，
申请(专利权)人：南昌航空大学，
类型：发明
国别省市：江西,36