本发明专利技术公开的抛光皮应用的聚氨酯配料，由所述聚氨酯配料由DMF、面胶、氧化铈及水性颜料组成，其中，DMF由二甲基甲酰胺及N,N‑二甲基乙酰胺组成，所述面胶由聚醚型聚酯、四氢呋喃及环己烷组成，DMF：45～54％，面胶29～36％，氧化铈，8～10％，水性颜料＝0.5～1.5％；可保障抛光皮的使用寿命大大增强，尤其是便于添加聚氨酯及氧化铈，有效实现高精度的抛光效果，获得更好的抛光效果，成分简单，可有效节约成本。

Polyurethane Ingredients for Polishing Skin

The polyurethane ingredient for polishing leather application disclosed by the invention consists of DMF, face glue, cerium oxide and water-borne pigments, in which DMF is composed of dimethylformamide and N, N dimethylacetamide. The face glue consists of polyether-type polyester, tetrahydrofuran and cyclohexane, DMF: 45-54%, face glue 29-36%, cerium oxide, 8-10%, water-borne pigments = 0.5-1. 5%. It can ensure that the service life of polishing skin is greatly enhanced, especially by adding polyurethane and cerium oxide. It can effectively achieve high-precision polishing effect, obtain better polishing effect, simple composition and effectively save cost.

【技术实现步骤摘要】
抛光皮应用的聚氨酯配料
本专利技术涉及抛光皮制造
，尤其涉及一种抛光皮应用的聚氨酯配料。
技术介绍
根据镜片的磨耗度的不同选择相应的肖式硬度的聚胺酯抛光皮，肖式硬度数值越大越硬。聚胺酯抛光皮里的填充物(氧化铈、氧化锆)的添加是微量加入，填充物的种类不决定所用的抛光粉，例如氧化铈可以与含有氧化锆填充剂的抛光皮配合使用或者相反。含有氧化铈的抛光皮---主要表现为提高抛光速率含有氧化锆的抛光皮---主要表现为提高光洁度不含有填充物的抛光皮---主要表现为抛光过程中的光圈稳定。抛光皮发泡孔多利于抛光粉的流动性、抛光速率要好。抛光皮发泡少的在亲水性能上要强。要实现高精度抛光效果且保障使用寿命的抛光皮设计，聚氨酯配料为其中的重要元素之一。
技术实现思路
为有效解决上述技术问题，本专利技术提供的抛光皮应用的聚氨酯配料，可满足技术需求，具体技术方案如下所述：抛光皮应用的聚氨酯配料，其特征在于，该方法包括以下步骤：所述聚氨酯配料由DMF、面胶、氧化铈及水性颜料组成，其中按照以下质量分数设定组分：其中，DMF由二甲基甲酰胺及N,N-二甲基乙酰胺组成，按以下质量分数设定组分：二甲基甲酰胺42～48％N,本文档来自技高网...

【技术保护点】
1.抛光皮应用的聚氨酯配料，其特征在于，该方法包括以下步骤：所述聚氨酯配料由DMF、面胶、氧化铈及水性颜料组成，其中按照以下质量分数设定组分：

【技术特征摘要】
1.抛光皮应用的聚氨酯配料，其特征在于，该方法包括以下步骤：所述聚氨酯配料由DMF、面胶、氧化铈及水性颜料组成，其中按照以下质量分数设定组分：其中，DMF由二甲基甲酰胺及N,N-二甲基乙酰胺组成，按以下质量分数设定组分：二甲基甲酰胺42～48％N,N-二甲基乙酰胺3～6％；所述面胶由聚醚型聚酯、四氢呋喃及环己烷组成，按以下质量分数设定组分：聚醚型聚酯21～25％四氢呋喃1～3％环己烷7～8％。2.如权利要求1所述的抛光皮应用的聚氨酯配料，其特征在于，该方法包括以下步骤：所述聚氨酯配料由DMF、面胶、氧化铈及水性颜料组成，其中按照以下质量分数设定组分：其中，DMF由二甲基甲酰胺及N,N-二甲基乙酰胺组成，按以...