A new method for preparing high damping material at room temperature and low pressure includes the following steps: S1: according to the proportion of butyl rubber 55-76.5%, phenolic resin 5-7%, zinc oxide 3-5%, stearic acid 1-1.5%, antioxidant 1.5-2%, modified silica filler 8-34.5%; S2: according to the proportion of each substance of S1, the above substances are selected according to the proportion of butyl rubber, zinc oxide and stearin. Acids, antioxidants, phenolic resins and modified silica fillers were added into the mixer in order to mix and produce sheets. S3: The mixtures in S2 were vulcanized by a flat vulcanizer.
【技术实现步骤摘要】
一种新型常温低压变高阻尼材料制备方法
本专利技术属于高性能阻尼材料领域，具体涉及一种新型常温低压变高阻尼材料制备方法。
技术介绍
橡胶材料是一种粘弹性材料，既能通过橡胶大分子间的内耗消耗能量，又能通过弹性形变储存并释放能量，可用于电子、精密仪器、汽车、船舶及航空航天等领域的阻尼减振材料。丁基橡胶是一种损耗因子较高的橡胶材料，由于其损耗因子高，对振动能量的耗散效果显著，是一种通用阻尼减振橡胶材料。但是通常情况下，较高的损耗因子意味着橡胶材料自身损耗模量较高，储能模量较低，压缩永久变形较大。而压缩永久变形性能对于阻尼减振产品而言，意味着结构的可靠性，是极其重要的性能指标。以应用为目的阻尼减振材料设计中为了保证压缩永久变形性能，通常会降低材料的损耗因子，导致丁基橡胶材料无法充分发挥其高阻尼的优势。随着技术的发展与革新，在电子、精密仪器、汽车、船舶及航空航天等领域，对阻尼减振产品也提出了更高的要求，除常温下具有较高的阻尼特性外，对其结构可靠性要求也越来越高。高阻尼丁基橡胶压缩永久变形性能差的缺点极大的限制了其在阻尼减振领域的进一步推广应用。因此，亟需改进现有材料体系，专利...
【技术保护点】
1.一种新型常温低压变高阻尼材料制备方法，其特征在于：包括以下步骤：S1：按照丁基橡胶55～76.5％，酚醛树脂5～7％，氧化锌3～5％，硬脂酸1～1.5％，防老剂1.5～2％，改性硅土填料8～34.5％的比例选取各组分；S2：按照S1的各物质比例，将以上物质按照丁基橡胶、氧化锌、硬脂酸、防老剂、酚醛树脂及改性硅土填料的顺序依次加入到开炼机中进行混炼、出片；S3：使用平板硫化机对S2中的混炼胶进行硫化成型。
【技术特征摘要】
1.一种新型常温低压变高阻尼材料制备方法，其特征在于：包括以下步骤：S1：按照丁基橡胶55～76.5％，酚醛树脂5～7％，氧化锌3～5％，硬脂酸1～1.5％，防老剂1.5～2％，改性硅土填料8～34.5％的比例选取各组分；S2：按照S1的各物质比例，将以上物质按照丁基橡胶、氧化锌、硬脂酸、防老剂、酚醛树脂及改性硅土填料的顺序依次加入到开炼机中进行混炼、出片；S3：使用平板硫化机对S2中的混炼胶进行硫化成型。2.根据权利要求1所述的一种新型常温低压变高阻尼材料制备方法，其特征在于：所述S2中，混炼时滚筒温度为40～60℃。3.根据权利要求2所述的一种新型常温低压变高阻尼材料制备方法，其特征在于：所述...
【专利技术属性】
技术研发人员：刘群策，赵鑫，张宇，苏红波，冯伟，