The invention discloses a method for preparing oxide ceramic powder by glycerol nitrate combustion, in which glycerol and metal nitrate solution are mixed, and the molar ratio of glycerol and metal ions is in the range of 0.70:1 to 0.94:1. Under heating conditions, the solution water evaporates and initiates combustion, and nitrate decomposes into oxides to obtain ceramic powders. This method can prepare a variety of oxide ceramic powders. It avoids the shortcomings of using a large amount of glycerol in traditional methods and has low cost. It can be used to prepare ceramic powders with high bulkiness and sintering activity, which are comparable to traditional methods.
【技术实现步骤摘要】
燃烧法制备陶瓷粉体的方法
本专利技术涉及一种以燃烧法制备氧化物陶瓷粉体的方法，具体过程是将硝酸盐水溶液与甘油混合，在加热条件下溶液水分挥发、引发燃烧，在燃烧过程导致的高温环境下，硝酸盐分解生成氧化物，得到陶瓷粉体。
技术介绍
燃烧法制备陶瓷粉体的基本过程是将陶瓷粉体对应的硝酸盐水溶液与燃烧助剂相混合，得到混合溶液。此混合溶液在加热升温过程中水分挥发，达到一定温度时燃烧助剂开始燃烧，燃烧导致的高温促使硝酸盐成分分解为氧化物，得到陶瓷粉体。已有研究报道中常用的燃烧助剂包括甘氨酸、柠檬酸、甘油、蔗糖、纤维素等。此方法制备的陶瓷粉体一般具有膨松的状态，呈现低的松装密度。一般而言，松装密度越低越好。在早期的燃烧法制备陶瓷粉体的经典文献A(MaterialsLetter,10(1990)6)中，研究人员以甘氨酸为燃烧助剂，指出了燃烧助剂的作用包括两个方面，一是提供燃烧反应的燃料，二是燃烧助剂的有机分子在溶液中与硝酸盐的金属离子相络合，在空间上分隔金属离子，从而导致硝酸盐分解形成氧化物时，可以形成细小的氧化物颗粒，并减少固体颗粒的团聚，获得颗粒小、分散性好、松装密度低的陶瓷粉体...
【技术保护点】
1.以燃烧法制备金属氧化物陶瓷粉体的方法，包括以下步骤：首先，根据金属氧化物陶瓷的化学式，以相应的金属硝酸盐为原料，配制水溶液；然后，在所述硝酸盐水溶液中加入甘油，均匀搅拌得到混合溶液；最后，所述混合溶液经加热、水分蒸发、引发燃烧等过程，生成金属氧化物陶瓷粉体；其特征在于：所述混合溶液中甘油与金属离子的摩尔比例在0.70:1到0.94:1范围内。
【技术特征摘要】
1.以燃烧法制备金属氧化物陶瓷粉体的方法，包括以下步骤：首先，根据金属氧化物陶瓷的化学式，以相应的金属硝酸盐为原料，配制水溶液；然后，在所述硝酸盐水溶液中加入甘油，均匀搅拌得到混合溶液；最后，所述混合溶液经加热、水分蒸发、引发燃烧等过程，生成金属氧化物陶瓷粉体；其特征在于：所述混合溶液中甘油与金属离子的摩尔比例在0.70:1到0.94:1范围内。2.如权利要求1所述的以燃烧法制备金属氧化物陶瓷粉体的方法，其特征在于，加热蒸发水分时的温度控制在100~150摄氏度。3.如权利要求1所述的以燃烧法制备金属氧化物陶瓷粉体的方法，其特征在于，引发燃烧时的温度控制在250~300摄氏度。4.如权利要求1所述的以燃烧法制备金属氧化物陶瓷粉体的方法，其特征在于，燃烧生成...
【专利技术属性】
技术研发人员：李海滨，李宝光，周公文，李阳，闫真，张诚然，王鹏，刘良禄，郝晓函，
申请(专利权)人：云南大学，
类型：发明