The invention provides a durable revitalizing stiffener which can remould the collapsed fabric skeleton. The preparation method comprises the following steps: (1) mixing and stirring polyvinyl alcohol and water in proportion of 1:30 to 20:1 of mass ratio; step (2) heating the mixture of polyvinyl alcohol and water until polyvinyl alcohol is completely dissolved; step (3): mixing polyethylene alcohol with water in proportion of 1:30 to 20:1; The mixture of enol and water is cooled to 65 The invention not only increases the elasticity and fullness of the fabric on the original basis, but also increases the durability and washability of the collapsed fabric because of its unique elasticity and fullness.
【技术实现步骤摘要】
一种可使塌掉的织物重塑骨架的耐久复活硬挺剂
本专利技术涉及织物护理剂
，具体为一种可使塌掉的织物重塑骨架的耐久复活硬挺剂。
技术介绍
国内硬挺剂市场主要以改性三聚氰胺甲醛树脂或三聚氰胺-尿素-甲醛树脂为主，这类硬挺剂中含有少量甲醛，可以满足大部分织物的硬挺加工整理。这类硬挺剂的传统生产工艺主要使用液体甲醛和三聚氰胺、尿素等原料经羟甲基化、缩聚和醚化改性等反应制备而成。由于液体甲醛中含有大量的水，在反应过程中醚化和缩聚等反应又有不少水产生，至反应结束时，体系中有大量水存在，硬挺剂的有效含量低，将其浓缩会消耗大量蒸汽，并产生大量难以处理的含甲醛废水，这些含甲醛废水处理成本高昂且难以彻底去除所含甲醛，很多硬挺剂生产企业为降低成本，将含甲醛废水只经过简单处理甚至不处理就直接排放，造成严重的环境污染。
技术实现思路
本专利技术所解决的技术问题在于提供一种可使塌掉的织物重塑骨架的耐久复活硬挺剂，以解决上述
技术介绍
中的问题。本专利技术所解决的技术问题采用以下技术方案来实现：一种可使塌掉的织物重塑骨架的耐久复活硬挺剂，其制备方法包括以下步骤：步骤(1)：将聚乙烯醇与水按照质量配...
【技术保护点】
1.一种可使塌掉的织物重塑骨架的耐久复活硬挺剂，其特征在于：其制备方法包括以下步骤：步骤(1)：将聚乙烯醇与水按照质量配比1：30至20：1的比例进行充分混合搅拌；步骤(2)：将聚乙烯醇与水的混合液升温至90℃，直至聚乙烯醇完全溶解；步骤(3)：将聚乙烯醇与水的混合液降温至65‑75℃，加十二烷基硫酸钠、引发剂、醋酸乙烯，本步骤中引发剂、醋酸乙烯加入总质量的一半，反应30分钟；步骤(4)：加入剩余引发剂和剩余醋酸乙烯，反应30分钟；步骤(5)：加入混合液质量的0.05‑0.2倍的邻苯二甲酸二甲酯，搅拌30分钟；步骤(6)：降温至20‑30℃，出料。
【技术特征摘要】
1.一种可使塌掉的织物重塑骨架的耐久复活硬挺剂，其特征在于：其制备方法包括以下步骤：步骤(1)：将聚乙烯醇与水按照质量配比1：30至20：1的比例进行充分混合搅拌；步骤(2)：将聚乙烯醇与水的混合液升温至90℃，直至聚乙烯醇完全溶解；步骤(3)：将聚乙烯醇与水的混合液降温至65-75℃，加十二烷基硫酸钠、引发剂、醋酸乙烯，本步骤中引发剂、醋酸乙烯加入总质量的一半，反应30分钟；步骤(4)：加入剩余引发剂和剩余醋酸乙烯，反应30分钟；步骤(5)：加入混合液质量的0.05-0.2倍的邻苯二甲酸二甲酯，搅拌30分钟；步骤(6)：降温至20-30℃，出料。2.根据权利要求1所述的一种可使塌掉的织物重塑骨...
【专利技术属性】
技术研发人员：张绍涛，
申请(专利权)人：纳派化学上海有限公司，
类型：发明
国别省市：上海,31
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。