The invention relates to a method for treating high-salt wastewater. First, the high-salt wastewater is put into an electrolysis reactor and electrolysed by a direct current power supply. Then, the electrolysed high-salt wastewater is filtered. After adding 4 6% removal agent of filtrate weight into the filtrate, it is stirred evenly, and finally filtered. The removal agent is activated carbon, Polyferrous sulfate and polyaluminium sulfate with a weight ratio of 1:1 1. 6:0.5 0.8. The method has the advantages of simple process, convenient operation, short reaction time, high efficiency of removing COD and total phosphorus, COD can be removed below 40 mg/L and total phosphorus can be removed below 0.8 mg/L.
【技术实现步骤摘要】
一种高盐废水的处理方法
本专利技术涉及一种高盐废水的处理方法,尤其是一种冶金工业高盐废水的处理方法,属于污水处理
技术介绍
随着我国钴、铜、镍等湿法冶炼技术的飞速发展,也带来了日益严重的环境污染问题,这主要表现在此类湿法冶炼工艺所产出的废水中,有机物污染浓度高、无机盐份高、生化性差,利用传统的一些化学法、物理法处理工艺难以实现COD、总磷的达标排放,且处理成本高,给企业节能减排带来极大的难度。目前高盐废水的处理方法中,去除剂加入量大,去除效率不高,200mg/L以下的COD,6mg/L以下的总磷去除率很低,无法达到排放标准,而且反应时间长,处理成本很高。
技术实现思路
本专利技术的目的是解决现有技术的不足,提供一种高盐废水的处理方法,工艺简单,操作方便,反应时间短,去除COD和总磷的效率高。技术方案一种高盐废水的处理方法,首先将高盐废水放入电解反应器,采用直流电源进行电解,然后将电解后的高盐废水过滤,往滤液中加入滤液重量的4-6%的去除剂后搅拌均匀,最后过滤,即可。所述去除剂由活性炭、聚合硫酸亚铁、聚合硫酸铝按重量比1:1-1.6:0.5-0.8组成。进一步,所述电解的电压为2~5v,电流为7~14A。进一步,所述去除剂由活性炭、聚合硫酸亚铁、聚合硫酸铝按重量比1:1.3:0.7组成。与现有技术相比,本专利技术的有益效果是:本专利技术的处理方法工艺简单,操作方便,反应时间短,去除COD和总磷的效率高,COD可以去除至40mg/L以下,总磷能除到0.8mg/L以下。具体实施方式下面结合具体实施例对本专利技术作进一步说明。实施例1取高盐废水2L,加入体积 ...
【技术保护点】
1.一种高盐废水的处理方法,其特征在于,首先将高盐废水放入电解反应器,采用直流电源进行电解,然后将电解后的高盐废水过滤,往滤液中加入滤液重量的4‑6%的去除剂后搅拌均匀,最后过滤,即可;所述去除剂由活性炭、聚合硫酸亚铁、聚合硫酸铝按重量比1:1‑1.6:0.5‑0.8组成。
【技术特征摘要】
1.一种高盐废水的处理方法,其特征在于,首先将高盐废水放入电解反应器,采用直流电源进行电解,然后将电解后的高盐废水过滤,往滤液中加入滤液重量的4-6%的去除剂后搅拌均匀,最后过滤,即可;所述去除剂由活性炭、聚合硫酸亚铁、聚合硫酸铝按重量比1:1-1.6...