The invention relates to a medicinal chlorinated butyl rubber stopper and its preparation process, belonging to the field of medicinal bottle stopper materials, which is prepared from 100 parts of chlorinated butyl rubber, 1.0 2.0 parts of cross-linking agent, 0.3 0.5 parts of acid absorbent, 50 80 parts of calcined kaolin, 5 10 parts of silica, 2 4 parts of polyethylene wax, 2 3 parts of titanium dioxide and 0.1 0.3 parts of carbon black. The invention relates to a medicinal chlorinated butyl rubber plug and a preparation method thereof. In the chemical performance test, the clarity is good, and there is no risk of drug contamination when the rubber plug contacts with the drug; using BSH as vulcanizing agent, using a small amount of magnesium oxide as acid absorbent, as vulcanizing system of medicinal chlorinated butyl rubber plug, it has good heat resistance.
【技术实现步骤摘要】
药用氯化丁基橡胶塞及其制备工艺
本专利技术涉及一种药用氯化丁基橡胶塞及其制备工艺，属于药用瓶塞材料领域。
技术介绍
目前最常用氯化丁基橡胶瓶塞采用的硫化体系为树脂氧化锌体系，但锌的采用不利于提升瓶塞的洁净度，特别是对PH值变化较大的药物的封装更为不利，另外考虑到氧化锌对某些药物的敏感性和配合禁忌问题，开发不需要氧化锌的硫化体系才是解决此问题的有效途径。交联剂BSH是一种不碳氮杂环双巯基盐，作为硫化剂应用于于氯化丁基橡胶时，不需要氧化锌即可对氯化丁基橡胶实现有效交联，同时可以提升产品的抗水、抗热和耐化学性。在与抗生素类药物，特别是酸碱性强的药物的试验中，相容性明显好于树脂氧化锌作为硫化体系的产品。也就是说交联剂BSH作为硫化剂的氯化丁基橡胶塞有更好的药物相容性。综上所述目前领域存在以下不足之处：1、目前常用的树脂硫化体系生产的氯化丁基橡胶活塞，在化学性能检测中澄清度不良，容易导致胶塞与药品接触时，使存在污染药品的风险；2、以树脂氧化锌作为硫化体系的氯化丁基橡胶塞存在耐热性差的问题；3、传统药用氯化丁基橡胶塞的树脂硫化体系需用氧化锌作为活性剂，不利于瓶塞的内在洁净度，...
【技术保护点】
1.一种药用氯化丁基橡胶塞，其特征在于由以下质量份数的原料制备而成；
【技术特征摘要】
1.一种药用氯化丁基橡胶塞，其特征在于由以下质量份数的原料制备而成；氯化丁基橡胶100交联剂1.0-2.0吸酸剂0.3-0.5煅烧高岭土50-80白炭黑5-10聚乙烯蜡2-4钛白粉2-3炭黑0.1-0.3。2.根据权利要求1所述的药用氯化丁基橡胶塞，其特征在于所述的：交联剂为碳氮杂环双巯基盐。3.根据权利要求1所述的药用氯化丁基橡胶塞，其特征在于所述的：吸酸剂为氧化镁。4.根据权利要求1所述的药用氯化丁基橡胶塞，其特征在于所述的：药用氯化丁基橡胶塞的制备工艺如下：原料配合→混炼→预成型→硫化成型→除边→清洗→包装；(1)混炼：进厂原料...
【专利技术属性】
技术研发人员：孟凡平，逯纪伟，杜彬，
申请(专利权)人：山东省药用玻璃股份有限公司，
类型：发明
国别省市：山东,37