The invention discloses a preparation method of two-dimensional alumina powder. The transparent aluminium sol was prepared by mixing aluminium salt, ammonia water and concentrated nitric acid in a certain proportion and reacting at a certain temperature. Then the aluminium sol was evenly coated on the surface modified base with a coater. After baking, the curing film was peeled off and the sheet powder was obtained. Two-dimensional alumina powder can be obtained by calcining flake powder at high temperature. The two-dimensional alumina powder obtained by the invention has the advantages of flat surface, smooth, compact, uniform thickness and large diameter-thickness ratio.
【技术实现步骤摘要】
一种二维氧化铝粉的制备方法
本专利技术涉及一种二维氧化铝粉的制备方法。
技术介绍
片状结构的二维氧化铝粉具有普通氧化铝熔点高、硬度大、耐腐蚀、绝缘性能好、机械强度大等优点，其特殊的二维片状结构、适中的表面活性、良好的附着力及显著的屏蔽效应，使其可广泛应用于散热材料、填充剂、增韧剂、耐火材料和珠光颜料等领域。目前二维氧化铝粉的主要制备方法有：熔盐法、机械粉碎法和水热法。熔盐法具有设备简单、生产周期短、产率高、成本低廉、产品形貌和粒径可控等优点，但粉片呈花瓣状，粉片杂乱堆集于一体。机械粉碎法虽然操作简单、成本低，但是得到的粉体纯度不高、粒径不均匀、形状不规则且表面粗糙，颗粒团聚现象严重。水热法制备的产物纯度高、粒径均匀且分散效果好，但其制备周期长，需要高温高压。专利CN108439465A(一种纳米二氧化钛溶胶的制备与负载方法)报道用钛源、溶剂、螯合剂、酸液和水制备溶胶，然后涂覆于基材上，通过风干和烧结得到纳米二氧化钛薄膜涂层；专利CN108149228A(一种CoFe2O4感光溶胶的制备方法以及CoFe2O4微细图形薄膜的制备方法)报道用钴盐、螯合剂、添加剂、铁盐等...
【技术保护点】
1.一种二维氧化铝粉的制备方法，其特征在于：步骤如下：S1.将铝盐溶于去离子水，边滴加氨水边搅拌，直至溶液变稠，生成白色沉淀；S2.将S1得到的白色沉淀进行洗涤、抽滤，得到滤饼，加入一定量的去离子水和浓硝酸，搅拌均匀，转移到三口烧瓶，通过调节反应时间、温度和搅拌器转速，制备出透明铝溶胶；S3.对基底用丙酮浸泡30min，然后用水冲洗，再将基底放置在一定浓度的氢氧化钠溶液中，80℃下水煮1h，用水冲洗，烘干待用；S4.将S2得到的铝溶胶用涂布器均匀涂布在S3得到的基底上，100℃下烘烤40min，剥离，再将剥离的粉体在1200℃下煅烧，得到二维氧化铝粉体。
【技术特征摘要】
1.一种二维氧化铝粉的制备方法，其特征在于：步骤如下：S1.将铝盐溶于去离子水，边滴加氨水边搅拌，直至溶液变稠，生成白色沉淀；S2.将S1得到的白色沉淀进行洗涤、抽滤，得到滤饼，加入一定量的去离子水和浓硝酸，搅拌均匀，转移到三口烧瓶，通过调节反应时间、温度和搅拌器转速，制备出透明铝溶胶；S3.对基底用丙酮浸泡30min，然后用水冲洗，再将基底放置在一定浓度的氢氧化钠溶液中，80℃下水煮1h，用水冲洗，烘干待用；S4.将S2得到的铝溶胶用涂布器均匀涂布在S3得到的基底上，100℃下烘烤40min，剥离，再将剥离的粉体在1200℃下煅烧，得到二维氧化铝粉体。2.根据权力要求1所述的制备方法，其特征在于，S1所述的铝盐为六水合氯化铝或硝酸铝。3.根据权力要求1所述的制...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。