The invention discloses a production method of modified urea-formaldehyde resin glue for cold pressing, which is characterized by the following specific quality components: formaldehyde 55%, urea 33%, polyvinyl alcohol 4%, melamine 5%, starch 1%, ammonia 2%. The preparation method is as follows: formaldehyde 55% is pumped into the reactor, PH is adjusted to 8.5, polyvinyl alcohol 4%, starch 1%, ammonia water 2% is added to raise the temperature to 88 degrees Celsius; It can hold for 30 minutes; adjust PH value 4.8, polycondensation reaction 20 minutes; adjust PH value 5.0 5.2, melamine 5%, reaction 10 minutes, urea 11%; reaction 20 minutes, adjust PH value 8.0, urea 11%; temperature down to 65, urea 11%; temperature down to 45.
【技术实现步骤摘要】
冷压用改性尿醛树脂胶水的生产方法及产品
本专利技术涉及脲醛树脂生产
，尤其是一种冷压用改性尿醛树脂胶水的生产方法及产品。
技术介绍
目前国内木料生产粘接主要以脲醛树脂胶为主，其工艺简单，成本较低、所以得到全面推广，但其甲醛释放量大，使用后的常常甲醛超标，但随着消费者环保意识的组建增强，国家环保政策的施行，生产相对较环保、甲醛释放量低的粘接胶，是企业发展的必由之路。
技术实现思路
本专利技术的目的在于为了克服现有技术的不足而提供一种成本较低、粘性好、甲醛释放量较低的冷压用改性尿醛树脂胶水。其具体质量组份如下：甲醛55%尿素33%聚乙烯醇4%三聚氰胺5%淀粉1%氨水2%其制备方法如下：a、甲醛55%抽入反应釜中，调节PH为8-8.5，加入聚乙烯醇4%、淀粉1%、氨水2%升温；b、升温到88℃停气，保温30分钟；c、调节PH值4.8，缩聚反应20分钟；d、调节PH值5.0-5.2，加三聚氰胺5%，反应10分钟，加尿素11%；e、反应20分钟，调节PH值为8.0，加尿素11%；f、温度降至65℃，加尿素11%；g、温度降至45℃出料。从本专利技术可以看出甲醛和尿素为主体...
【技术保护点】
1.冷压用改性尿醛树脂胶水的生产方法，其特征在于：其具体质量组份如下：甲醛55%，尿素33%，聚乙烯醇4%，三聚氰胺5%，淀粉1%，氨水2%，其制备方法如下：（a）甲醛55%抽入反应釜中，调节PH为8‑8.5，加入聚乙烯醇4%、淀粉1%、氨水2%升温；（b）升温到88℃停气，保温30分钟；（c）调节PH值4.8，缩聚反应20分钟；（d）调节PH值5.0‑5.2，加三聚氰胺5%，反应10分钟，加尿素11%；（e）反应20分钟，调节PH值为8.0，加尿素11%；（f）温度降至65℃，加尿素11%；（g）温度降至45℃出料。
【技术特征摘要】
1.冷压用改性尿醛树脂胶水的生产方法，其特征在于：其具体质量组份如下：甲醛55%，尿素33%，聚乙烯醇4%，三聚氰胺5%，淀粉1%，氨水2%，其制备方法如下：（a）甲醛55%抽入反应釜中，调节PH为8-8.5，加入聚乙烯醇4%、淀粉1%、氨水2%升温；（b）升温到88℃停气，保温30分钟；（c）调节PH...
【专利技术属性】
技术研发人员：何龙江，杨铁勋，何凤娟，何静，黄梓珈，贾伟君，
申请(专利权)人：南充市龙煌建材有限公司，
类型：发明
国别省市：四川,51