The invention discloses a silver bromide tin dioxide composite nanomaterial, whose molar ratio is 5%-10% of silver bromide and 90%-95% of tin dioxide. A preparation method of AgCl4.5H2O, KBr and urea is also disclosed. The mixed solution A is obtained by dissolving SnCl4.5H2O, KBr and urea in deionized water. AgNO3 solution is added to the mixed solution A while stirring in water bath at 80-90 ~C. The magnetic stirring reaction lasts for 2.5-3.5h. The precipitate is obtained. The precipitate is centrifuged, washed, alcohol washed and dried in oven at 55-65 ~C. Silver bromide and tin dioxide composite nanomaterials were obtained by mid-drying. The silver bromide tin dioxide composite nanomaterial prepared by the method of the invention has good visible light absorption, remarkably improves the separation of photogenerated carriers, and greatly improves the photocatalytic performance of the material.
【技术实现步骤摘要】
一种溴化银二氧化锡复合纳米材料及其制备方法
本专利技术涉及材料
，特别是涉及一种溴化银二氧化锡复合纳米材料及其制备方法。
技术介绍
近年来，卤化银(AgX，X＝Cl，Br，I)负载的SiO2或TiO2基底材料具有很好的可见光光催化活性。值得注意的是，由于载流子得到有效的分离，载体上的卤化银能够稳定存在，避免了相应的光腐蚀。在光的照射下，卤化银部分还原出纳米银。这样，得到的银/卤化银体系由于纳米银的表面等离子体效应而具有强烈的可见光光吸收，同时，该体系显示出了良好的光催化性能。不过，直接沉淀上的卤化银不可避免地带来严重的团聚，这样妨碍了界面电荷的转移。因此，设计合成纳米级的具有高催化活性和稳定性的卤化银纳米粒子，对科学研究和实际应用都是必要的。
技术实现思路
本专利技术的目的在于提供一种溴化银二氧化锡复合纳米材料的制备方法，以克服现有技术中的不足。为实现上述目的，本专利技术提供如下技术方案：本专利技术公开一种溴化银二氧化锡复合纳米材料，其摩尔比组成为：溴化银5％～10％，二氧化锡90％～95％。本专利技术还公开一种溴化银二氧化锡复合纳米材料的制备方法，包括：将Sn...
【技术保护点】
1.一种溴化银二氧化锡复合纳米材料，其特征在于，其摩尔比组成为：溴化银5％～10％，二氧化锡90％～95％。
【技术特征摘要】
1.一种溴化银二氧化锡复合纳米材料，其特征在于，其摩尔比组成为：溴化银5％～10％，二氧化锡90％～95％。2.一种溴化银二氧化锡复合纳米材料的制备方法，其特征在于，包括：将SnCl4·5H2O、KBr和尿素溶于去离子水中，获得混合溶液A，于80～90℃水浴条件下边搅拌边向混合溶液A中滴加AgNO3溶液，磁力搅拌反应2.5～3.5h，获得沉淀物，将沉淀物离心、水洗、醇洗，并于55～65℃烘箱中烘干，获得溴化银二氧化锡复合纳米材料。3.根据权利要求2所述的溴化银二氧化锡复合纳米材料的制备方法，其特征在于，所述SnCl4·5H2O的制备方法包括：(1)先将金属锡...
【专利技术属性】
技术研发人员：黄俊，
申请(专利权)人：张家港市沐和新材料技术开发有限公司，
类型：发明
国别省市：江苏,32