The invention relates to a high nitrogen wear-resistant and corrosion-resistant alloy and a preparation method thereof, belonging to the technical field of ferroalloy materials. The high nitrogen wear-resistant and corrosion-resistant alloy of the invention consists of the following elements: C: 2.1 2.5%, Cr: 23 28%, Mo: 0.5 0.8%, Si: 0.9 1.2%, Mn: 0.5 0.8%, N: 0.2 0.6%, P < 0.01%, S < 0.01%, the remainder is iron and inevitable impurities. The high nitrogen wear-resisting and corrosion-resisting alloy of the invention has high content of carbon, chromium and nitrogen elements, good corrosion-resisting and wear-resisting performance, and is suitable for being used as impeller material of slurry pump.
【技术实现步骤摘要】
一种高氮耐磨耐蚀合金及其制备方法
本专利技术涉及一种高氮耐磨耐蚀合金及其制备方法，属于铁合金材料
技术介绍
机械装备的性能与其制造材料的性能密切相关。渣浆泵是广泛用于矿山、电力、冶金、煤炭、环保等行业的输送含有磨蚀性固体颗粒浆体的工业泵，如冶金选矿厂用于浆料输送，火电厂用于水力除灰等。由于大部分情况下输送的料浆中含有腐蚀介质，再加上固体颗粒的磨损，在料浆泵的转子高速旋转过程中，腐蚀和磨损同时作用，使叶轮的表面损坏十分严重，大大缩短了工件使用寿命。由此可知，渣浆泵的损坏甚至失效的原因是腐蚀磨损，腐蚀磨损通常是指腐蚀环境中摩擦表面出现的材料流失现象。腐蚀磨损过程中，金属材料在承受摩擦力(表面切应力)的同时还与环境介质发生化学或者电化学反应从而导致材料出现流失。腐蚀磨损过程中的腐蚀行为与磨损行为与单独的腐蚀或者磨损有较大的不同，腐蚀可以加速磨损，磨损也可以促进腐蚀，从而加速了材料的破坏。因此，腐蚀磨损已成为材料损坏或设备失效的重要原因之一，为了解决这个问题，就要求制造渣浆泵的材料在具有较好耐磨性的同时具有良好的耐腐蚀性。目前，广泛使用的渣浆泵叶轮材料主要由高铬...
【技术保护点】
1.一种高氮耐磨耐蚀合金，其特征在于，由如下质量百分比的元素组成：C：2.1‑2.5％、Cr：23‑28％、Mo：0.5‑0.8％、Si：0.9‑1.2％、Mn：0.5‑0.8％、N：0.2‑0.6％、P≤0.01％、S≤0.01％，余量为铁及不可避免的杂质。
【技术特征摘要】
1.一种高氮耐磨耐蚀合金，其特征在于，由如下质量百分比的元素组成：C：2.1-2.5％、Cr：23-28％、Mo：0.5-0.8％、Si：0.9-1.2％、Mn：0.5-0.8％、N：0.2-0.6％、P≤0.01％、S≤0.01％，余量为铁及不可避免的杂质。2.根据权利要求1所述的高氮耐磨耐蚀合金，其特征在于，由如下质量百分比的元素组成：C：2.2-2.5％、Cr：23-28％、Mo：0.5-0.8％、Si：0.9-1.2％、Mn：0.5-0.8％、N：0.2-0.6％、P≤0.01％、S≤0.01％，余量为铁及不可避免的杂质。3.根据权利要求1所述的高氮耐磨耐蚀合金，其特征在于，由如下质量百分比的元素组成：C：2.1-2.5％、Cr：23-28％、Mo：0.5-0.8％、Si：0.9-1.2％、Mn：0.5-0.8％、N：0.2-0.6％、P≤0.01％、S≤0.01％，稀土元素：0.1-0.3％，余量为铁及不可避免的杂质。4.一种高氮耐磨耐蚀合金的制备方法，其特征在于，包括如下步骤：1)将Fe原料、Mn原料、Cr原料真空熔炼得熔炼液，然后加入Si原料、C原料、氮...
【专利技术属性】
技术研发人员：魏世忠，路富刚，徐流杰，王晓东，肖利强，周玉成，王方方，易旭阳，毛丰，陈冲，张程，潘昆明，李秀青，
申请(专利权)人：河南科技大学，
类型：发明
国别省市：河南,41