The invention relates to an indole azobenzene/graphene composite solar energy heat storage material, in which the monomer indole azo molecule is covalently bonded to the surface of graphene, and one azo molecule is grafted on every 30-50 carbon atoms. The preparation method is as follows: preparation of azo molecule; partial reduction of graphene oxide: graphene oxide is oxidized by sodium carbonate with a mass fraction of 20%-30%. Aqueous solution adjusts pH to 7 9, adding pH-adjusted graphene oxide aqueous solution in sodium borohydride solution, and placed at 75 90 Celsius. After centrifugal filtration, partially reduced graphene oxide is obtained, and then re-dispersed in water by ultrasound. Grafting graphene with azobenzene: adding indole-type azobenzene with equal molar amount of sodium nitrite into deionized water, in ice bath The diazo salts were prepared by adding hydrochloric acid slowly under the conditions. The diazo salts were slowly added to the diazo salts to obtain partially reduced graphene oxide and reacted in ice bath for one day.
【技术实现步骤摘要】
一种吲哚偶氮苯/石墨烯复合太阳能储热材料及其制备方法
本专利技术是一种吲哚偶氮苯/石墨烯复合太阳能储热材料及其制备方法，该材料在未来可用于光热存储和太阳能利用等方面的高新应用中，属于复合材料领域。
技术介绍
随着社会的不断发展，环境污染已经成为每个国家都需要面对的问题，生活中现在常用的石油能源对环境的破坏极其严重。为了解决环境问题，我们需要开发一种新型绿色能源用于取代现在所使用的高污染且即将用尽的石油资源。太阳能是一种地球上最为丰富的能源，每小时所提供的能量超过了人类2001年全球能源消耗总和，虽然人类在一直依靠植物的光合作用对太阳能进行利用，但是现在对太阳能的利用依然很少。现在对太阳能的利用多采用太阳能光伏或太阳能电池，然而这些方法能量转换次数过多，能量转换效率低。若利用光热材料直接储存能量则可以将能量转化效率大幅提高。偶氮苯作为一种光致异构化的染料，是一种前景很好的光热储能材料。偶氮苯稳定的反式结构会在紫外光作用下变为顺式偶氮苯，并且将能量储存在化学键中，在一定刺激下又可以将能量释放，并且回到稳定结构。然而传统偶氮苯的缺点在于其成膜性能差，能量密度低以及半衰期...
【技术保护点】
1.一种吲哚偶氮苯/石墨烯复合太阳能储热材料，其单体的吲哚偶氮分子以共价键方式接枝到石墨烯表面，每30～50个碳原子接枝一个偶氮分子，结构式如下：
【技术特征摘要】
1.一种吲哚偶氮苯/石墨烯复合太阳能储热材料，其单体的吲哚偶氮分子以共价键方式接枝到石墨烯表面，每30～50个碳原子接枝一个偶氮分子，结构式如下：2.权利要求1所述的吲哚偶氮苯/石墨烯复合太阳能储热材料的制备方法，步骤如下：1)偶氮分子的制备：将的3-氨基-5氯吲哚加入带蒸馏水的烧杯中，用的盐酸将其溶解，溶解后在冰浴条件下加入亚硝酸钠溶液，冰浴反应1-3小时，制得重氮盐，加入1-2当量的3,5二甲氧基苯胺并在氩气氛围中反应，得到吲哚型偶氮苯单体，其中，3-氨基-5氯吲哚，盐酸和亚硝酸钠的摩尔比为1：(3-4)：(1.05-1.2)。2)...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。