The invention discloses a high impact waterproof polyester powder coating, which relates to the field of coating. The high impact waterproof polyester powder coating of the invention comprises the following quality components: carboxyl-terminated polyester resin 40-60 mass fraction, epoxy resin 20-30 mass fraction, alkyd resin 10-20 mass fraction, carbon fiber 4-16 mass fraction, zinc oxide 3-8 mass fraction, composite filler 20-40 mass fraction, curing agent 4-7 mass fraction, dispersant 0.4-0.6 mass fraction, additive 0.6-0.8 mass fraction and antimicrobial property. The dosage ranges from 1 to 5 parts. The high impact waterproof polyester powder coating has broad application prospects by mixing, melting extrusion, pressing, crushing and screening the raw material components of the high impact waterproof polyester powder coating.
【技术实现步骤摘要】
一种高抗冲防水聚酯粉末涂料及其制备方法
本专利技术涉及涂料领域，尤其涉及一种高抗冲防水聚酯粉末涂料及其制备方法。
技术介绍
涂料在实际生活中的应用十分广泛，其中粉末涂料由于具有无公害、机械强度好、效率高、可回收和节能等优良性能被广泛应用。纯聚酯型粉末涂料用途广泛，一般用于交通器材和农用工具中，这类涂料有很好的耐候性，但是由于其中有酯基结构的存在，在潮湿的环境中水解，其机械性能下降，粉末涂料表现出很差抗冲击性能，从而出现软化或掉落的情况。
技术实现思路
针对上述存在的问题，本专利技术提供一种高抗冲防水聚酯粉末涂料及其制备方法，通过所述配方及方法制得具有高抗冲性和防水性的聚酯粉末涂料。本专利技术采用的技术方案如下：一种高抗冲防水聚酯粉末涂料，包括以下质量份的成分：端羧基聚酯树脂40~60质量份，环氧树脂20~30质量份、醇酸树脂10~20质量份、碳纤维4~16质量份、氧化锌3~8质量份、复合填料20~40质量份、固化剂4~7质量份、分散剂0.4~0.6质量份、助剂0.6~0.8质量份和抗菌剂1~5质量份。进一步地，所述环氧树脂为双酚S型环氧树脂和酚醛环氧树脂的混合物，其中...
【技术保护点】
1.一种高抗冲防水聚酯粉末涂料，其特征在于，包括以下质量份的成分：端羧基聚酯树脂40~60质量份，环氧树脂20~30质量份、醇酸树脂10~20质量份、碳纤维4~16质量份、氧化锌3~8质量份、复合填料20~40质量份、固化剂4~7质量份、分散剂0.4~0.6质量份、助剂0.6~0.8质量份和抗菌剂1~5质量份。
【技术特征摘要】
1.一种高抗冲防水聚酯粉末涂料，其特征在于，包括以下质量份的成分：端羧基聚酯树脂40~60质量份，环氧树脂20~30质量份、醇酸树脂10~20质量份、碳纤维4~16质量份、氧化锌3~8质量份、复合填料20~40质量份、固化剂4~7质量份、分散剂0.4~0.6质量份、助剂0.6~0.8质量份和抗菌剂1~5质量份。2.如权利要求1所述的一种高抗冲防水聚酯粉末涂料，其特征在于，所述环氧树脂为双酚S型环氧树脂和酚醛环氧树脂的混合物，其中，所述双酚S型环氧树脂的质量百分比为30~35%。3.如权利要求1所述的一种高抗冲防水聚酯粉末涂料，其特征在于，所述复合填料的成分包括以下质量份：轻质碳酸钙20~28质量份、滑石粉25~30质量份、石英粉25~30质量份、凹凸棒...
【专利技术属性】
技术研发人员：范沈杰，
申请(专利权)人：湖州吴兴道场城乡建设发展有限公司，
类型：发明
国别省市：浙江,33