The invention belongs to the technical field of macromolecule composite materials, and specifically relates to low warpage glass fiber reinforced polypropylene composite materials and its preparation method. It is prepared from the following raw materials according to the mass percentage ratio: glass fiber reinforced polypropylene modified granular materials 95.0 99.9%, thermal expansion microspheres 0.1 5.0%, totally 100%, after mixing, injection moulding according to conventional injection process conditions. The low warpage glass fiber reinforced polypropylene composite material provided by the invention and the preparation method can effectively improve the warpage problem of injection moulding parts while maintaining the basic performance index of the glass fiber reinforced polypropylene composite material.
【技术实现步骤摘要】
低翘曲玻纤增强聚丙烯复合材料及其制备方法
本专利技术属于高分子复合材料
，具体涉及低翘曲玻纤增强聚丙烯复合材料及其制备方法。
技术介绍
聚丙烯(PP)材料具有良好的加工性能及比较高的性价比。但是纯聚丙烯材料刚性比较低、耐冲击性能差。因此对于一些有高刚性高抗冲有要求的应用，如汽车仪表板骨架，天窗骨架、尾门板，常常需要加入玻纤作为增强填料。一般作为增强填料的短玻纤长度为1-4毫米长，长玻纤长度为8-15毫米，直径均为10-20微米左右，长径比超过100。而其他常用增强填料如滑石粉和碳酸钙的典型长径比分别为20和1左右，通常粒径均为7微米左右。因此，增强玻纤的长径比远高于其他常用非纤维状增强填料。玻纤如此高的长径比常常使被增强的高分子基料在注塑过程中产生比较强的分子链取向,导致取向内应力。另外，玻纤增强聚丙烯的热传导系数仅仅比纯聚丙烯高一些，不及滑石粉填充聚丙烯的三分之一。这容易导致冷却定型时候收缩不均匀而产生冷却内应力。因此这两种内应力的存在往往使玻纤增强聚丙烯注塑件产生翘曲。
技术实现思路
针对上述技术问题，本专利技术的目的是提供一种低翘曲玻纤增强聚丙烯复合材料的...
【技术保护点】
1.低翘曲玻纤增强聚丙烯复合材料，其特征在于，包括以下原料按照质量百分数配比制备而成：玻纤增强聚丙烯改性颗粒料95.0‑99.9％，热膨胀微球0.1‑5.0％，合计100％。
【技术特征摘要】
1.低翘曲玻纤增强聚丙烯复合材料，其特征在于，包括以下原料按照质量百分数配比制备而成：玻纤增强聚丙烯改性颗粒料95.0-99.9％，热膨胀微球0.1-5.0％，合计100％。2.根据权利要求1所述的低翘曲玻纤增强聚丙烯复合材料，其特征在于，所述的玻纤增强聚丙烯改性颗粒料，包括以下原料按照质量份数配比制备所得：聚丙烯35～90份，玻璃纤维10～65份，相容剂0.1-10份，抗氧剂及紫外吸收剂0.1～0.8份，润滑剂0.1～0.5份。3.根据权利要求2所述的低翘曲玻纤增强聚丙烯复合材料，其特征在于，所述的聚丙烯为均聚聚丙烯或共聚聚丙烯。4.根据权利要求2所述的低翘曲玻纤增强聚丙烯复合材料，其特征在于，所述的玻璃纤维，为短玻璃纤维、长玻璃纤维或玻璃纤维母粒。5.根据权利要求2所...
【专利技术属性】
技术研发人员：金闪，赵茜菁，石耀琦，
申请(专利权)人：苏州禾昌聚合材料股份有限公司，
类型：发明
国别省市：江苏,32