The invention provides a construction waste and slag fine powder preform and a manufacturing method thereof. The raw materials of the construction waste and slag fine powder preform include the following components: construction waste and slag fine powder: 50 80%; domestic waste: 1 5%; cement: 5 15%; water: 5 9.6%; fly ash: 0.5 4%; high efficiency water reducing agent: 1 3%; defoamer: 0.1 0.5%; Silica fume: 0.5 1%. The construction waste and slag powder prefabricated parts provided by the invention can replace concrete prefabricated parts to become building materials with high strength such as floor tiles, cut blocks or curb stones, and realize harmless treatment of construction waste and slag powder at low cost, with good economic and social benefits.
【技术实现步骤摘要】
一种建筑垃圾与矿渣微粉预制件及其制造方法
本专利技术涉及一种建筑垃圾与矿渣微粉预制件及其制造方法，特别是利用建筑垃圾与矿渣微粉制成的地砖和砌块，属于绿色建材制造领域。
技术介绍
随着我国现代化建设步伐的加快,建筑垃圾与矿渣微粉正在日益增加。相对于生活垃圾,我国的建筑垃圾与矿渣微粉的再利用没有引起多大重视,绝大部分未经任何处理便被运往郊外露天堆放或填埋,而堆放和填埋则需耗用大量的征地、垃圾清运等建设资金,同时清运和堆放过程中的遗撒和扬尘又加重了环境污染。我国建筑垃圾与矿渣微粉的数量已占到城市垃圾总量的30％-40％。以500-600吨/万平方米的标准推算，到2020年，我国还将新增建筑面积约300亿平方米，新产生的建筑垃圾与矿渣微粉将是一个令人震撼的数字。然而，绝大部分建筑垃圾与矿渣微粉未经任何处理，便被施工单位运往郊外或乡村，露天堆放或填埋，耗用大量的征用土地费、垃圾清运费等建设经费，同时，清运和堆放过程中的遗撒和粉尘、灰砂飞扬等问题又造成了严重的环境污染。而目前我国如此巨量的建筑垃圾与矿渣微粉绝大部分未经任何处理，便运往郊外或乡村，采用随意露天堆放或直接填埋的方...
【技术保护点】
1.一种建筑垃圾与矿渣微粉预制件及其制造方法，其特征在于该所述的混凝土渠槽预制件包括以下重量份数的原料：建筑垃圾与矿渣微粉：50‑80％水泥：5‑15％水：5‑9.6％生活垃圾：1‑5％粉煤灰：0.5‑4％高效减水剂：1‑3％消泡剂：0.1‑0.5％
【技术特征摘要】
1.一种建筑垃圾与矿渣微粉预制件及其制造方法，其特征在于该所述的混凝土渠槽预制件包括以下重量份数的原料：建筑垃圾与矿渣微粉：50-80％水泥：5-15％水：5-9.6％生活垃圾：1-5％粉煤灰：0.5-4％高效减水剂：1-3％消泡剂：0.1-0.5％2.如权利要求1所述的建筑垃圾与矿渣微粉预制件，利用建筑垃圾与矿渣微粉生产制造预制件，其特征在于：制备方法为将建筑垃圾与矿渣微粉送入破碎机进行破碎，然后输出到分拣装置，通过分拣装置对建筑垃圾与矿渣微粉中的杂物进行分拣去除，并将分拣后的建筑垃圾与矿渣微粉输出到磁选装置进行磁选，将磁选后的建筑垃圾与矿渣微粉输出到振动筛，用振动筛对建筑垃圾与矿渣微粉进行筛分后，进入破碎、制砂、干燥的工序。3.根据权利要求2所述的建筑垃圾与矿渣微粉预制件，利用建筑垃圾与矿渣微粉...
【专利技术属性】
技术研发人员：刘朝辉，
申请(专利权)人：遵义市旭辉新型节能建材有限公司，
类型：发明
国别省市：贵州,52