The invention relates to a method of using ultra-fine fly ash to make environmental protection bricks, in which the raw materials for producing environmental protection bricks by using ultra-fine fly ash include the following components: ultra-fine fly ash: 50 80%; domestic waste: 1 5%; cement: 5 15%; water: 5 9.6%; accelerator gypsum: 1 3%; activator silica fume: 0.1 0.5%; water reducer: 0.1 0.1 15%; 5%; foaming stabilizer, chlorate: 0.5 1%. The invention has simple process, the product density is 300-700 kg/m3, the strength is 2.5-7 MPa, and meets the national quality requirements. It can be used as either non-load-bearing wall brick or external wall load-bearing brick. The invention realizes the harmless treatment of industrial waste at a lower cost, and has good economic and social benefits.
【技术实现步骤摘要】
一种利用超精细粉煤粉灰烧制环保砖的方法
本专利技术涉及一种利用超精细粉煤粉灰烧制环保砖的方法，特别是利用超精细粉煤粉灰制成的环保砖，属于绿色建材制造领域。
技术介绍
超精细粉煤粉灰是燃煤电厂排出的经静电集尘器收集得到的物质。燃煤形成的灰渣中超精细粉煤粉灰约占4/5,底灰约占1/5。依据煤源及种类不同,形成的超精细粉煤粉灰有显著差异。我国是以煤炭为主要能源的国家，电力的76％由煤炭产生，燃煤产生的超精细粉煤粉灰总堆存量已超过10亿t，而且还在以每年0.8亿～1亿t的速度增加，成为世界上最大的排灰国[1]。超精细粉煤粉灰存放不仅占用大量土地，还会造成严重的环境污染。开展超精细粉煤粉灰等煤系固体废弃物综合利用，延伸煤炭产业链，不仅关系到中国煤炭产业、电力工业及相关工业可持续发展问题，而且对保护土地资源，减少、消除污染，实现循环经济具有重要意义。
技术实现思路
本专利技术的目的在于，提供一种利用超精细粉煤粉灰烧制环保砖的方法。本专利技术的环保砖既可作非承重墙砖,也可作外墙承重砖，同时，操作相对简单，减少了人员和成本的投入，且利用超精细粉煤粉灰或者生活垃圾作为原料在很大程度上降...
【技术保护点】
1.一种利用超精细粉煤粉灰烧制环保砖的方法，其特征在于，是由原超精细粉煤粉灰、生活垃圾、水泥、水、促凝剂石膏、活性剂硅灰、发泡稳定剂、减水剂氯酸盐组成，在每lOOKg原料中，、促凝剂石膏0.8～1.OKg,促凝剂石膏0.9～1.lKg、活化剂硅灰0.9～1.lKg发泡稳定剂18～20Kg,其余为水泥、超精细粉煤粉灰或生活垃圾，水泥与超精细粉煤粉灰或生活垃圾的质量比1:1。
【技术特征摘要】
1.一种利用超精细粉煤粉灰烧制环保砖的方法，其特征在于，是由原超精细粉煤粉灰、生活垃圾、水泥、水、促凝剂石膏、活性剂硅灰、发泡稳定剂、减水剂氯酸盐组成，在每lOOKg原料中，、促凝剂石膏0.8～1.OKg,促凝剂石膏0.9～1.lKg、活化剂硅灰0.9～1.lKg发泡稳定剂18～20Kg,其余为水泥、超精细粉煤粉灰或生活垃圾，水泥与超精细粉煤粉灰或生活垃圾的质量比1:1。2.如权利要求1所述的一种利用超精细粉煤粉灰烧制环保砖的方法...