A process of glass-coated stainless steel wire production is introduced. The stainless steel wire after removing grease is immersed in the glass melting pool under the condition of gas protection. In the melting pool, the glass is coated on the surface of stainless steel wire, and the wire is drawn from the hole of the composite die. The outline of the composite die is conical structure, in order to establish the hydrodynamic lubrication condition between the composite die and the stainless steel wire, and then compound it. The die outlet is cooled to glass-coated stainless steel wire. The process is suitable for the production of circular and flat glass-coated stainless steel wire, and the cross-sectional area of glass-coated stainless steel wire is less than 2 mm.
【技术实现步骤摘要】
一种玻璃包覆不锈钢丝的生产工艺
本专利技术涉及到复合丝材制造工艺的领域，特别涉及到一种玻璃包覆不锈钢丝的生产工艺。
技术介绍
由于现代信息技术的迅猛发展，在电子领域越来越需要小尺寸、高灵敏度和快速响应的传感器及线圈，而这离不开高精度、高性能的绝缘包覆金属复合丝，传统的漆包线由于耐热性和绝缘性难以满足高性能线圈的需要。近年来，通过熔融纺丝法制备玻璃包覆金属丝，则较好的解决了复合丝的热稳定性和小尺寸的问题。但，采用熔融纺丝法制备玻璃包覆金属微丝需要电磁场悬浮金属熔池，因此金属熔池的质量小（为几克数量等级），导致熔融纺丝工艺的稳定控制难度高，复合丝及金属芯丝尺寸规格难以稳定，且难以制备较大直径的玻璃包覆金属丝（直径为0.1mm数量级）。采用芯丝直径波动范围较大的玻璃包覆复合丝制备高性能的电子产品，则会降低其产品的灵敏度及精度。
技术实现思路
针对以上熔融纺丝制备玻璃包覆不锈钢丝存在的不足，本专利技术提供一种玻璃包覆不锈钢丝的生产工艺，该原理为：把去除油脂后的不锈钢丝在气体保护条件下浸入玻璃熔池中，在融池中玻璃包覆在不锈钢丝表面后，并从复合模具孔中拉丝成型，复合模具轮廓采用锥...
【技术保护点】
1.一种玻璃包覆不锈钢丝的生产工艺，期特征在于：把去除油脂后的不锈钢丝在气体保护条件下浸入玻璃熔池中，在融池中玻璃包覆在不锈钢丝表面后，并从复合模具孔中拉丝成型，复合模具轮廓采用锥形结构，以期在复合模具和不锈钢丝之间建立流体动力润滑条件，然后在复合模具出口经冷却制成玻璃包覆不锈钢丝。
【技术特征摘要】
1.一种玻璃包覆不锈钢丝的生产工艺，期特征在于：把去除油脂后的不锈钢丝在气体保护条件下浸入玻璃熔池中，在融池中玻璃包覆在不锈钢丝表面后，并从复合模具孔中拉丝成型，复合模具轮廓采用锥形结构，以期在复合模具和不锈钢丝之间建立流体动力润滑条件，然后在复合模具出口经冷却制成玻璃包覆不锈钢丝。2.一种玻璃包覆不锈钢丝的生产工艺，该工艺适于圆形、扁平等断面玻璃包覆不锈钢丝的生产，且玻璃包...